Franklinite Pavese A, Levy D, Hoser A American Mineralogist 85 (2000) 1497-1502 Cation distribution in synthetic zinc ferrite (Zn0.97Fe2.02O4) from in situ high temperature neutron powder diffraction Sample at T = 800 K _database_code_amcsd 0002579 CELL PARAMETERS: 8.4785 8.4785 8.4785 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 609.477 Density (g/cm3): 5.250 MAX. ABS. INTENSITY / VOLUME**2: 98.13643508 RIR: 6.086 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.12 4.81 4.8951 1 1 1 8 29.81 35.93 2.9976 2 2 0 12 35.10 100.00 2.5564 3 1 1 24 36.72 7.44 2.4475 2 2 2 8 42.66 13.42 2.1196 4 0 0 6 52.90 11.60 1.7307 4 2 2 24 56.39 26.60 1.6317 5 1 1 24 56.39 5.37 1.6317 3 3 3 8 61.91 36.49 1.4988 4 4 0 12 70.21 3.98 1.3406 6 2 0 24 73.20 7.99 1.2930 5 3 3 24 74.19 3.18 1.2782 6 2 2 24 78.09 1.32 1.2238 4 4 4 8 85.75 4.47 1.1330 6 4 2 48 88.60 6.71 1.1038 7 3 1 48 88.60 4.96 1.1038 5 5 3 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.