Ulvospinel Yamanaka T, Kyono A, Nakamoto Y, Meng Y, Kharlamova S, Struzhkin V V, Mao H American Mineralogist 98 (2013) 736-744 High-pressure phase transitions of Fe3-xTixO4 solid solution up to 60 GPa correlated with electronic spin transition Locality: synthetic Note: P = 14 GPa _database_code_amcsd 0019931 CELL PARAMETERS: 5.9052 5.9052 8.1834 90.000 90.000 90.000 SPACE GROUP: I4_1/amd X-RAY WAVELENGTH: 1.541838 Cell Volume: 285.367 Density (g/cm3): 5.203 MAX. ABS. INTENSITY / VOLUME**2: 47.98084516 RIR: 3.003 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.53 38.91 4.7886 1 0 1 8 30.27 13.18 2.9526 2 0 0 4 30.59 23.63 2.9225 1 1 2 8 35.73 100.00 2.5133 2 1 1 16 36.28 59.64 2.4764 1 0 3 8 37.57 17.70 2.3943 2 0 2 8 43.34 30.48 2.0878 2 2 0 4 44.27 15.03 2.0459 0 0 4 2 47.95 2.03 1.8974 2 1 3 16 53.97 7.37 1.6988 3 1 2 16 54.57 3.29 1.6816 2 0 4 8 57.38 31.88 1.6060 3 2 1 16 57.76 7.94 1.5962 3 0 3 8 58.52 12.71 1.5772 1 0 5 8 62.96 22.19 1.4763 4 0 0 4 63.68 43.77 1.4612 2 2 4 8 66.25 1.68 1.4108 4 1 1 16 66.60 2.52 1.4042 3 2 3 16 71.44 1.06 1.3204 4 2 0 8 71.61 1.27 1.3177 3 3 2 8 72.97 1.19 1.2965 1 1 6 8 74.88 9.72 1.2681 4 1 3 16 75.55 3.35 1.2585 3 0 5 8 75.68 6.16 1.2566 4 2 2 16 77.02 2.48 1.2382 2 0 6 8 80.18 5.57 1.1972 4 0 4 8 83.50 1.25 1.1577 3 2 5 16 87.55 1.40 1.1143 5 1 2 16 88.04 1.61 1.1094 4 2 4 16 88.84 1.35 1.1014 3 1 6 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.