Cs4[(UO2)3O(MoO4)2(MoO5)] Krivovichev S V, Burns P C The Canadian Mineralogist 40 (2002) 201-209 Crystal chemistry of uranyl molybdates. VI. New uranyl molybdate units in the structures of Cs4[(UO2)3O(MoO4)2(MoO5)] and Cs6[(UO2)(MoO4)4] _database_code_amcsd 0005765 7.510 7.897 9.774 79.279 81.269 87.251 P1 atom x y z Uiso U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3) U(1) .01499 .85419 .80084 .0126 .0160 .0131 .0086 -.0009 -.0030 -.0008 U(2) -.02434 .01907 .14717 .0118 .0162 .0090 .0104 -.0006 -.0030 -.0017 U(3) -.01698 .53349 .15619 .0111 .0148 .0084 .0103 -.0001 -.0034 -.0014 Mo(1) -.0832 .1966 .4992 .0150 .0192 .0139 .0116 -.0006 -.0044 .0005 Mo(2) -.1489 .3483 .8845 .0166 .0262 .0107 .0147 .0011 -.0095 -.0022 Mo(3) .2000 .7235 .4407 .0131 .0127 .0163 .0105 -.0001 -.0031 -.0020 Cs(1) -.5249 .2528 .2754 .0251 .0231 .0212 .0325 .0024 -.0085 -.0056 Cs(2) -.3163 .7101 .5148 .0313 .0181 .0458 .0304 -.0049 -.0070 -.0043 Cs(3) .4843 .7837 .0417 .0269 .0182 .0338 .0266 -.0004 -.0035 .0000 Cs(4) .3548 .2762 .7544 .0456 .0357 .057 .0424 -.0170 -.0091 .0010 O(1) -.258 .966 .193 .021 .021 .017 .027 -.004 -.006 -.002 O(2) .219 .487 .109 .022 .021 .024 .023 .000 -.003 -.009 O(3) -.048 .125 .906 .022 .037 .014 .017 -.003 -.008 -.005 O(4) -.253 .578 .216 .024 .025 .022 .024 .006 -.001 -.005 O(5) .259 .854 .791 .022 .013 .039 .012 .006 -.001 -.002 O(6) .054 .731 .601 .021 .027 .021 .017 .000 -.004 -.008 O(7) .073 .740 .293 .015 .018 .014 .013 .000 -.008 .002 O(8) .050 .101 .630 .017 .025 .012 .012 -.005 -.004 .004 O(9) .332 .540 .462 .030 .029 .028 .034 .013 -.013 -.008 O(10) -.221 .862 .793 .020 .013 .026 .026 .002 -.007 -.016 O(11) -.104 .291 .113 .018 .023 .014 .019 -.003 -.006 -.003 O(12) -.031 .546 .902 .021 .039 .006 .018 .001 -.010 .001 O(13) -.043 .050 .382 .040 .08 .025 .014 .003 -.009 -.002 O(14) .006 .801 .029 .019 .037 .010 .009 -.001 -.002 -.001 O(15) -.133 .385 .703 .044 .10 .014 .019 -.004 -.025 -.001 O(16) .350 .890 .405 .025 .024 .030 .017 -.012 -.001 .007 O(17) -.009 .394 .396 .028 .05 .020 .015 -.007 -.012 .003 O(18) .212 .070 .105 .025 .024 .013 .033 -.003 -.003 .008 O(19) -.376 .356 .939 .041 .023 .04 .06 -.004 -.016 -.008 O(20) -.310 .200 .549 .043 .023 .07 .024 -.011 -.005 .013