Harmotome Stuckenschmidt E, Fuess H, Kvick A European Journal of Mineralogy 2 (1990) 861-874 Investigation of the structure of harmotome by X-ray (293 K, 100 K) and neutron diffraction (15 K) Sample: 100 K _database_code_amcsd 0006410 9.841 14.085 8.680 90 124.78 90 P2_1/m atom x y z occ Biso U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3) Ba .8661 1/4 .1958 .98 .0160 .0076 .0137 0 .0089 0 SiT1 .7370 .0264 .2844 .65 .51 .0070 .0055 .0067 -.0003 .0028 -.0008 AlT1 .7370 .0264 .2844 .35 .51 .0070 .0055 .0067 -.0003 .0028 -.0008 SiT2 .4221 .1416 .0123 .84 .43 .0046 .0025 .0092 .0015 .0031 -.0005 AlT2 .4221 .1416 .0123 .16 .43 .0046 .0025 .0092 .0015 .0031 -.0005 SiT3 .0596 .0060 .2917 .70 .62 .0085 .0076 .0073 .0005 .0046 .0015 AlT3 .0596 .0060 .2917 .30 .62 .0085 .0076 .0073 .0005 .0046 .0015 SiT4 .1247 .1387 .0383 .77 .58 .0090 .0053 .0079 .0016 .0055 .0012 AlT4 .1247 .1387 .0383 .23 .58 .0090 .0053 .0079 .0016 .0055 .0012 O1 .1058 .0858 .1922 2.63 .0337 .0297 .0263 -.0078 .0201 .0053 O2 .6460 .5717 .1649 1.07 .0158 .0070 .0178 .0004 .0085 .0040 O3 .6159 .1223 .1753 .82 .0110 .0062 .0138 .0021 .0059 .0016 O4 .0015 .9054 .1751 1.38 .0168 .0190 .0165 .0007 .0065 -.0036 O5 .9091 .0532 .3005 .94 .0116 .0141 .0099 .0035 .0043 .0054 O6 .3183 .3689 .1038 1.42 .0149 .0213 .0178 -.0071 .0106 -.0051 O7 .7764 .4830 .4952 1.19 .0150 .0146 .0156 -.0021 .0099 -.0009 O8 .5956 3/4 .0660 1.09 .0177 .0017 .0221 0 .0131 0 O9 .0728 1/4 .0328 1.79 .0167 .0205 .0306 0 .0164 0 O10 .8033 3/4 .4971 2.78 .0336 .0438 .0282 0 .0103 0 O20 .1085 3/4 .4592 2.33 .0517 .0188 .0180 0 .0155 0 O30 .2971 .8633 .1275 3.73 .0570 .0513 .0335 -.0071 .0281 -.0139 O40 .5027 1/4 .4855 13.5 .221 .246 .0595 0 .010 0 O50 .4926 .565 .4661 6.5 .0389 .137 .0721 .0165 .0328 .047