Hedenbergite Redhammer G J, Amthauer G, Lottermoser W, Treutmann W European Journal of Mineralogy 12 (2000) 105-120 Synthesis and structural properties of clinopyroxenes of the hedenbergite CaFeSi2O6 - aegirine NaFeSi2O6 solid-solution series Sample: hd/6 _database_code_amcsd 0006815 CELL PARAMETERS: 9.8475 9.0277 5.2495 90.000 104.805 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 451.189 Density (g/cm3): 3.637 MAX. ABS. INTENSITY / VOLUME**2: 19.43062776 RIR: 1.740 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.52 24.42 6.5509 1 1 0 4 18.64 8.70 4.7603 2 0 0 2 19.67 5.66 4.5139 0 2 0 2 20.16 2.73 4.4044 -1 1 1 4 27.23 9.94 3.2754 2 2 0 4 29.75 100.00 3.0031 -2 2 1 4 29.84 36.66 2.9939 3 1 0 4 30.80 10.02 2.9031 -3 1 1 4 34.71 34.34 2.5845 -1 3 1 4 35.12 48.88 2.5550 2 2 1 4 35.37 41.32 2.5376 0 0 2 2 35.62 1.59 2.5202 -1 1 2 4 37.80 3.27 2.3801 4 0 0 2 38.41 4.03 2.3433 3 1 1 4 39.95 1.18 2.2569 0 4 0 2 40.31 13.94 2.2375 1 1 2 4 40.69 1.03 2.2173 -3 1 2 4 40.79 2.34 2.2120 0 2 2 4 41.35 4.36 2.1836 3 3 0 4 42.07 22.09 2.1476 -3 3 1 4 42.61 13.25 2.1218 -4 2 1 4 43.90 5.06 2.0622 0 4 1 4 44.55 9.16 2.0339 2 0 2 2 45.08 12.18 2.0113 -4 0 2 2 45.88 2.99 1.9780 -1 3 2 4 46.12 1.90 1.9683 -2 4 1 4 48.18 5.80 1.8889 3 3 1 4 48.88 1.07 1.8631 5 1 0 4 49.13 1.23 1.8544 2 2 2 4 49.77 1.58 1.8321 1 3 2 4 49.99 2.34 1.8244 2 4 1 4 50.55 3.92 1.8056 4 2 1 4 51.52 15.18 1.7739 1 5 0 4 52.60 1.83 1.7399 3 1 2 4 53.94 1.29 1.7000 -1 5 1 4 54.40 5.83 1.6864 0 4 2 4 55.58 1.73 1.6534 -3 1 3 4 56.11 14.00 1.6392 -5 3 1 4 56.16 4.78 1.6377 4 4 0 4 56.68 16.72 1.6240 -2 2 3 4 58.14 5.05 1.5868 6 0 0 2 58.84 5.96 1.5693 3 5 0 4 59.67 5.90 1.5496 4 0 2 2 60.08 3.16 1.5401 -6 2 1 4 60.38 5.05 1.5330 -6 0 2 2 61.44 11.79 1.5090 -1 3 3 4 61.64 4.86 1.5046 0 6 0 2 62.13 1.49 1.4939 -4 2 3 4 62.43 1.34 1.4875 -1 5 2 4 63.35 1.85 1.4681 -3 3 3 4 63.47 1.01 1.4657 4 2 2 4 64.41 17.15 1.4465 5 3 1 4 65.64 5.67 1.4224 1 5 2 4 65.91 8.57 1.4172 -3 5 2 4 66.26 1.04 1.4105 1 3 3 4 66.52 4.71 1.4057 2 2 3 4 68.02 1.52 1.3783 -2 4 3 4 69.64 4.15 1.3502 6 2 1 4 69.95 2.31 1.3449 7 1 0 4 70.47 5.61 1.3362 -7 1 2 4 71.69 4.21 1.3165 -5 3 3 4 73.12 5.90 1.2942 0 6 2 4 73.74 3.53 1.2848 -3 1 4 4 74.24 1.07 1.2775 4 4 2 4 74.83 3.44 1.2688 0 0 4 2 75.09 6.72 1.2651 3 5 2 4 75.35 2.17 1.2614 -4 0 4 2 76.19 1.59 1.2495 -1 7 1 4 77.67 2.31 1.2294 1 7 1 4 80.75 1.83 1.1901 8 0 0 2 80.98 1.29 1.1873 -8 2 1 4 84.76 2.84 1.1437 -6 0 4 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.