Aegirine Redhammer G J, Amthauer G, Lottermoser W, Treutmann W European Journal of Mineralogy 12 (2000) 105-120 Synthesis and structural properties of clinopyroxenes of the hedenbergite CaFeSi2O6 - aegirine NaFeSi2O6 solid-solution series Sample: ae60/1 _database_code_amcsd 0006821 CELL PARAMETERS: 9.7189 8.8818 5.2835 90.000 106.598 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 437.075 Density (g/cm3): 3.614 MAX. ABS. INTENSITY / VOLUME**2: 18.91258124 RIR: 1.704 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.78 31.31 6.4277 1 1 0 4 19.06 5.30 4.6570 2 0 0 2 19.99 10.98 4.4409 0 2 0 2 20.07 10.12 4.4240 -1 1 1 4 24.43 4.28 3.6436 1 1 1 4 27.76 7.69 3.2139 2 2 0 4 29.85 100.00 2.9935 -2 2 1 4 30.50 42.50 2.9308 3 1 0 4 30.86 6.54 2.8978 -3 1 1 4 35.04 28.18 2.5607 -1 3 1 4 35.45 2.17 2.5319 -1 1 2 4 35.46 39.91 2.5317 0 0 2 2 35.93 41.18 2.4996 2 2 1 4 38.67 1.67 2.3285 4 0 0 2 39.46 3.15 2.2835 3 1 1 4 40.31 1.08 2.2374 -3 1 2 4 40.80 15.03 2.2116 1 1 2 4 41.04 2.36 2.1994 0 2 2 4 42.18 2.38 2.1426 3 3 0 4 42.45 20.60 2.1296 -3 3 1 4 42.97 12.24 2.1049 -4 2 1 4 44.56 6.31 2.0335 0 4 1 4 44.72 11.26 2.0263 -4 0 2 2 45.40 7.32 1.9976 2 0 2 2 46.05 1.17 1.9710 -1 3 2 4 46.64 3.87 1.9473 -2 4 1 4 48.09 2.16 1.8922 -5 1 1 4 49.34 4.22 1.8468 3 3 1 4 49.44 1.41 1.8435 -4 2 2 4 50.03 1.07 1.8231 5 1 0 4 51.03 2.05 1.7898 2 4 1 4 51.94 3.51 1.7606 4 2 1 4 52.44 13.38 1.7449 1 5 0 4 53.86 2.89 1.7022 3 1 2 4 54.97 1.20 1.6703 -3 1 3 4 55.01 6.39 1.6693 0 4 2 4 56.35 16.72 1.6326 -2 2 3 4 56.81 14.71 1.6207 -5 3 1 4 57.34 6.26 1.6069 4 4 0 4 59.55 4.47 1.5523 6 0 0 2 60.00 5.31 1.5418 3 5 0 4 60.39 4.83 1.5328 -6 0 2 2 60.89 2.89 1.5214 -6 2 1 4 61.31 4.98 1.5121 4 0 2 2 61.54 11.27 1.5070 -1 3 3 4 61.57 1.42 1.5062 -4 2 3 4 62.77 4.93 1.4803 0 6 0 2 63.04 2.00 1.4747 -3 3 3 4 63.07 1.03 1.4740 -1 5 2 4 63.83 1.26 1.4583 -5 1 3 4 65.17 1.61 1.4314 4 2 2 4 66.20 15.67 1.4116 5 3 1 4 66.36 8.73 1.4086 -3 5 2 4 66.71 3.73 1.4021 1 5 2 4 67.59 4.57 1.3860 2 2 3 4 68.08 2.28 1.3771 -2 4 3 4 70.75 6.81 1.3316 -7 1 2 4 71.30 3.91 1.3227 -5 3 3 4 71.72 3.46 1.3160 6 2 1 4 71.73 2.15 1.3159 7 1 0 4 72.99 4.31 1.2963 -3 1 4 4 74.04 1.07 1.2803 -2 6 2 4 74.21 7.07 1.2779 0 6 2 4 74.37 2.07 1.2755 -4 0 4 2 75.04 3.53 1.2658 0 0 4 2 76.17 1.21 1.2498 4 4 2 4 76.81 6.94 1.2410 3 5 2 4 77.52 1.72 1.2313 -1 7 1 4 79.21 2.41 1.2093 1 7 1 4 82.44 1.30 1.1700 -8 2 1 4 82.93 1.42 1.1642 8 0 0 2 83.66 2.94 1.1560 -6 0 4 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.