LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 175 K _database_code_amcsd 0007305 CELL PARAMETERS: 9.5161 8.5708 5.2397 90.000 109.920 90.000 SPACE GROUP: P2_1/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 401.784 Density (g/cm3): 3.782 MAX. ABS. INTENSITY / VOLUME**2: 20.44274110 RIR: 1.760 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.31 81.91 6.1891 1 1 0 4 19.85 4.46 4.4734 2 0 0 2 20.22 45.99 4.3915 -1 1 1 4 20.73 30.75 4.2854 0 2 0 2 25.63 38.91 3.4758 1 1 1 4 30.27 100.00 2.9526 -2 2 1 4 31.77 67.10 2.8166 3 1 0 4 32.91 8.47 2.7215 1 3 0 4 35.92 6.56 2.4999 -1 1 2 4 36.01 23.12 2.4941 -1 3 1 4 36.48 33.47 2.4631 0 0 2 2 37.80 30.69 2.3799 2 2 1 4 38.49 1.17 2.3391 -2 3 1 4 39.45 2.66 2.2841 1 3 1 4 40.14 3.65 2.2467 -3 1 2 4 41.11 2.23 2.1958 -2 2 2 4 41.19 1.78 2.1914 1 0 2 2 42.17 3.05 2.1427 0 4 0 2 42.58 18.96 2.1231 1 1 2 4 43.37 20.76 2.0861 -3 3 1 4 43.76 11.37 2.0685 -4 2 1 4 44.48 9.29 2.0369 -4 0 2 2 46.20 1.17 1.9649 0 4 1 4 47.02 2.02 1.9325 2 4 0 4 47.84 5.34 1.9012 2 0 2 2 47.97 14.17 1.8964 -2 4 1 4 49.04 8.04 1.8575 -5 1 1 4 49.55 3.41 1.8396 -4 2 2 4 50.58 2.95 1.8047 -3 3 2 4 51.93 1.90 1.7608 3 3 1 4 53.42 4.34 1.7152 2 4 1 4 54.32 1.26 1.6889 -1 1 3 4 54.51 8.28 1.6835 1 5 0 4 54.89 4.65 1.6727 4 2 1 4 56.95 18.44 1.6168 -2 2 3 4 56.96 9.12 1.6166 0 4 2 4 57.04 10.14 1.6145 3 1 2 4 58.13 2.49 1.5870 -4 4 1 4 58.26 18.15 1.5836 -5 3 1 4 59.77 8.38 1.5473 4 4 0 4 60.66 4.62 1.5267 -6 0 2 2 61.49 1.09 1.5081 -4 2 3 4 61.77 3.47 1.5018 1 1 3 4 61.85 2.75 1.5000 5 1 1 4 62.26 4.04 1.4911 6 0 0 2 62.33 1.27 1.4897 -2 3 3 4 62.49 2.47 1.4863 -6 2 1 4 62.49 6.46 1.4862 3 5 0 4 62.96 2.78 1.4763 -4 4 2 4 63.01 9.35 1.4752 -1 3 3 4 63.42 4.15 1.4666 -5 1 3 4 63.56 2.46 1.4638 -3 3 3 4 65.07 1.88 1.4334 -1 5 2 4 65.20 2.94 1.4309 4 0 2 2 65.32 7.29 1.4285 0 6 0 2 67.60 1.14 1.3858 4 4 1 4 67.90 7.53 1.3804 -3 5 2 4 69.22 1.88 1.3572 4 2 2 4 69.44 6.55 1.3535 -2 4 3 4 69.64 1.05 1.3502 1 5 2 4 69.77 1.90 1.3480 -2 6 1 4 69.91 3.22 1.3456 1 3 3 4 69.99 16.21 1.3443 5 3 1 4 71.05 3.48 1.3268 2 2 3 4 71.46 4.11 1.3201 -5 3 3 4 71.49 9.63 1.3197 -7 1 2 4 73.32 4.18 1.2912 -3 1 4 4 74.17 3.66 1.2784 -4 0 4 2 75.16 2.96 1.2641 7 1 0 4 76.03 1.91 1.2518 6 2 1 4 76.64 1.47 1.2434 -6 4 2 4 77.20 7.98 1.2357 0 6 2 4 77.51 2.05 1.2316 0 0 4 2 79.64 1.00 1.2039 4 6 0 4 80.70 1.88 1.1907 -1 7 1 4 80.76 1.13 1.1900 4 4 2 4 81.05 6.53 1.1865 3 5 2 4 82.47 1.24 1.1695 -4 6 2 4 82.82 2.66 1.1655 1 7 1 4 82.95 2.17 1.1640 -6 0 4 2 84.91 1.22 1.1420 2 6 2 4 85.24 1.11 1.1385 -8 -2 1 4 87.16 1.01 1.1183 8 0 0 2 89.21 1.14 1.0979 -4 4 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.