LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 200 K _database_code_amcsd 0007306 CELL PARAMETERS: 9.5189 8.5722 5.2428 90.000 109.930 90.000 SPACE GROUP: P2_1/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 402.180 Density (g/cm3): 3.779 MAX. ABS. INTENSITY / VOLUME**2: 20.45732950 RIR: 1.763 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.31 82.10 6.1903 1 1 0 4 19.84 4.48 4.4744 2 0 0 2 20.21 45.86 4.3936 -1 1 1 4 20.72 30.80 4.2861 0 2 0 2 25.62 39.03 3.4770 1 1 1 4 30.26 100.00 2.9535 -2 2 1 4 31.76 66.90 2.8172 3 1 0 4 32.90 8.53 2.7220 1 3 0 4 35.90 6.57 2.5013 -1 1 2 4 36.00 22.98 2.4948 -1 3 1 4 36.46 33.26 2.4644 0 0 2 2 37.79 30.54 2.3805 2 2 1 4 38.48 1.06 2.3397 -2 3 1 4 39.44 2.71 2.2846 1 3 1 4 40.11 3.59 2.2478 -3 1 2 4 41.09 2.26 2.1968 -2 2 2 4 41.18 1.58 2.1923 1 0 2 2 42.17 2.99 2.1430 0 4 0 2 42.56 19.04 2.1240 1 1 2 4 43.36 20.59 2.0867 -3 3 1 4 43.75 11.24 2.0692 -4 2 1 4 44.46 9.29 2.0378 -4 0 2 2 46.19 1.19 1.9653 0 4 1 4 47.01 2.00 1.9328 2 4 0 4 47.82 5.33 1.9020 2 0 2 2 47.96 14.23 1.8968 -2 4 1 4 49.03 7.98 1.8580 -5 1 1 4 49.53 3.44 1.8404 -4 2 2 4 50.55 2.96 1.8055 -3 3 2 4 51.92 1.85 1.7612 3 3 1 4 53.41 4.28 1.7156 2 4 1 4 54.29 1.26 1.6898 -1 1 3 4 54.50 8.26 1.6838 1 5 0 4 54.87 4.62 1.6731 4 2 1 4 56.92 18.34 1.6177 -2 2 3 4 56.94 9.19 1.6171 0 4 2 4 57.02 10.09 1.6150 3 1 2 4 58.11 2.47 1.5874 -4 4 1 4 58.25 18.12 1.5840 -5 3 1 4 59.75 8.38 1.5476 4 4 0 4 60.63 4.55 1.5273 -6 0 2 2 61.45 1.08 1.5089 -4 2 3 4 61.74 3.46 1.5025 1 1 3 4 61.84 2.71 1.5003 5 1 1 4 62.25 3.97 1.4915 6 0 0 2 62.29 1.13 1.4904 -2 3 3 4 62.47 2.48 1.4867 -6 2 1 4 62.48 6.36 1.4864 3 5 0 4 62.94 2.77 1.4768 -4 4 2 4 62.98 9.35 1.4759 -1 3 3 4 63.39 4.12 1.4674 -5 1 3 4 63.52 2.51 1.4645 -3 3 3 4 65.05 1.87 1.4338 -1 5 2 4 65.18 2.97 1.4313 4 0 2 2 65.31 7.15 1.4287 0 6 0 2 67.59 1.15 1.3860 4 4 1 4 67.88 7.56 1.3808 -3 5 2 4 69.20 1.90 1.3576 4 2 2 4 69.41 6.49 1.3540 -2 4 3 4 69.62 1.01 1.3505 1 5 2 4 69.75 1.88 1.3483 -2 6 1 4 69.87 3.19 1.3462 1 3 3 4 69.97 16.02 1.3446 5 3 1 4 71.01 3.52 1.3273 2 2 3 4 71.42 4.08 1.3207 -5 3 3 4 71.46 9.58 1.3202 -7 1 2 4 73.27 4.22 1.2919 -3 1 4 4 74.12 3.69 1.2792 -4 0 4 2 75.14 2.93 1.2644 7 1 0 4 76.01 1.90 1.2521 6 2 1 4 76.61 1.47 1.2437 -6 4 2 4 77.18 7.98 1.2360 0 6 2 4 77.46 2.06 1.2322 0 0 4 2 79.62 1.03 1.2041 4 6 0 4 80.68 1.86 1.1910 -1 7 1 4 80.73 1.10 1.1903 4 4 2 4 81.02 6.51 1.1868 3 5 2 4 82.45 1.22 1.1698 -4 6 2 4 82.80 2.61 1.1657 1 7 1 4 82.89 2.17 1.1647 -6 0 4 2 84.89 1.21 1.1423 2 6 2 4 85.22 1.09 1.1388 -8 -2 1 4 89.15 1.15 1.0984 -4 4 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.