LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 225 K _database_code_amcsd 0007307 CELL PARAMETERS: 9.5193 8.5713 5.2466 90.000 109.990 90.000 SPACE GROUP: P2_1/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 402.294 Density (g/cm3): 3.778 MAX. ABS. INTENSITY / VOLUME**2: 20.59314265 RIR: 1.775 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.31 81.61 6.1890 1 1 0 4 19.85 4.34 4.4729 2 0 0 2 20.20 45.68 4.3962 -1 1 1 4 20.73 30.72 4.2856 0 2 0 2 25.62 38.83 3.4764 1 1 1 4 30.25 100.00 2.9545 -2 2 1 4 31.77 66.21 2.8164 3 1 0 4 32.91 8.49 2.7217 1 3 0 4 35.88 6.49 2.5028 -1 1 2 4 36.00 22.57 2.4951 -1 3 1 4 36.45 33.22 2.4653 0 0 2 2 37.80 30.19 2.3798 2 2 1 4 39.45 2.78 2.2843 1 3 1 4 40.08 3.48 2.2496 -3 1 2 4 41.06 2.29 2.1981 -2 2 2 4 41.17 1.40 2.1924 1 0 2 2 42.17 2.92 2.1428 0 4 0 2 42.56 19.07 2.1240 1 1 2 4 43.36 20.29 2.0870 -3 3 1 4 43.74 11.10 2.0694 -4 2 1 4 44.42 9.25 2.0393 -4 0 2 2 46.19 1.23 1.9652 0 4 1 4 47.02 2.01 1.9325 2 4 0 4 47.83 5.21 1.9016 2 0 2 2 47.96 14.24 1.8969 -2 4 1 4 49.03 7.98 1.8581 -5 1 1 4 49.50 3.44 1.8414 -4 2 2 4 50.53 2.99 1.8063 -3 3 2 4 51.94 1.85 1.7606 3 3 1 4 53.42 4.15 1.7152 2 4 1 4 54.25 1.29 1.6907 -1 1 3 4 54.50 8.25 1.6836 1 5 0 4 54.90 4.56 1.6724 4 2 1 4 56.88 18.25 1.6187 -2 2 3 4 56.94 9.18 1.6173 0 4 2 4 57.04 9.98 1.6145 3 1 2 4 58.11 2.43 1.5874 -4 4 1 4 58.24 17.99 1.5841 -5 3 1 4 59.77 8.34 1.5472 4 4 0 4 60.61 4.47 1.5279 -6 0 2 2 61.40 1.07 1.5100 -4 2 3 4 61.73 3.47 1.5027 1 1 3 4 61.87 2.69 1.4997 5 1 1 4 62.27 3.92 1.4910 6 0 0 2 62.47 2.47 1.4867 -6 2 1 4 62.49 6.25 1.4862 3 5 0 4 62.92 2.75 1.4772 -4 4 2 4 62.95 9.29 1.4765 -1 3 3 4 63.33 4.08 1.4685 -5 1 3 4 63.48 2.59 1.4654 -3 3 3 4 65.04 1.86 1.4340 -1 5 2 4 65.21 2.94 1.4308 4 0 2 2 65.32 6.97 1.4285 0 6 0 2 67.61 1.14 1.3856 4 4 1 4 67.86 7.62 1.3811 -3 5 2 4 69.23 1.93 1.3572 4 2 2 4 69.38 6.39 1.3546 -2 4 3 4 69.75 1.83 1.3482 -2 6 1 4 69.87 3.10 1.3463 1 3 3 4 70.00 15.70 1.3441 5 3 1 4 71.02 3.54 1.3273 2 2 3 4 71.37 4.05 1.3215 -5 3 3 4 71.43 9.54 1.3206 -7 1 2 4 73.21 4.28 1.2929 -3 1 4 4 74.05 3.72 1.2803 -4 0 4 2 75.17 2.90 1.2640 7 1 0 4 76.05 1.89 1.2515 6 2 1 4 76.59 1.48 1.2440 -6 4 2 4 77.18 8.00 1.2360 0 6 2 4 77.43 2.09 1.2326 0 0 4 2 79.64 1.04 1.2039 4 6 0 4 80.68 1.84 1.1909 -1 7 1 4 80.76 1.09 1.1899 4 4 2 4 81.04 6.50 1.1865 3 5 2 4 82.43 1.19 1.1700 -4 6 2 4 82.81 2.20 1.1656 -6 0 4 2 82.82 2.55 1.1656 1 7 1 4 84.90 1.18 1.1422 2 6 2 4 85.23 1.08 1.1386 -8 -2 1 4 89.08 1.18 1.0991 -4 4 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.