LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 303 K _database_code_amcsd 0007311 CELL PARAMETERS: 9.5613 8.5691 5.2668 90.000 110.248 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 404.852 Density (g/cm3): 3.754 MAX. ABS. INTENSITY / VOLUME**2: 21.19952372 RIR: 1.839 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.29 81.61 6.1963 1 1 0 4 19.79 3.73 4.4852 2 0 0 2 20.13 43.08 4.4114 -1 1 1 4 20.73 30.31 4.2846 0 2 0 2 25.60 37.63 3.4791 1 1 1 4 30.16 100.00 2.9629 -2 2 1 4 31.69 63.32 2.8232 3 1 0 4 32.91 8.84 2.7217 1 3 0 4 35.76 6.07 2.5107 -1 1 2 4 35.96 19.96 2.4974 -1 3 1 4 36.36 33.38 2.4707 0 0 2 2 37.78 27.84 2.3812 2 2 1 4 39.44 3.36 2.2848 1 3 1 4 39.87 2.90 2.2611 -3 1 2 4 40.91 2.90 2.2057 -2 2 2 4 42.18 2.53 2.1423 0 4 0 2 42.51 20.00 2.1267 1 1 2 4 43.25 18.99 2.0919 -3 3 1 4 43.58 10.10 2.0770 -4 2 1 4 44.16 8.94 2.0510 -4 0 2 2 46.19 1.28 1.9655 0 4 1 4 47.01 2.00 1.9331 2 4 0 4 47.78 4.61 1.9035 2 0 2 2 47.91 15.13 1.8989 -2 4 1 4 48.80 8.11 1.8661 -5 1 1 4 49.26 3.49 1.8499 -4 2 2 4 50.36 2.93 1.8121 -3 3 2 4 51.90 1.98 1.7617 3 3 1 4 52.74 1.02 1.7356 -5 1 2 4 53.41 3.65 1.7155 2 4 1 4 54.08 1.46 1.6956 -1 1 3 4 54.51 8.32 1.6834 1 5 0 4 54.83 4.19 1.6743 4 2 1 4 56.67 17.42 1.6242 -2 2 3 4 56.89 9.15 1.6186 0 4 2 4 56.99 9.65 1.6159 3 1 2 4 57.98 2.32 1.5907 -4 4 1 4 58.05 17.72 1.5889 -5 3 1 4 59.69 8.14 1.5491 4 4 0 4 60.25 3.92 1.5361 -6 0 2 2 61.08 1.06 1.5170 -4 2 3 4 61.63 3.48 1.5050 1 1 3 4 61.77 2.55 1.5019 5 1 1 4 62.08 3.56 1.4951 6 0 0 2 62.21 2.59 1.4922 -6 2 1 4 62.46 5.44 1.4869 3 5 0 4 62.71 2.68 1.4815 -4 4 2 4 62.80 9.32 1.4797 -1 3 3 4 62.95 3.87 1.4766 -5 1 3 4 63.24 3.29 1.4705 -3 3 3 4 64.98 1.92 1.4352 -1 5 2 4 65.14 2.90 1.4321 4 0 2 2 65.34 5.95 1.4282 0 6 0 2 67.56 1.23 1.3866 4 4 1 4 67.73 7.86 1.3835 -3 5 2 4 69.16 2.20 1.3582 4 2 2 4 69.20 5.88 1.3577 -2 4 3 4 69.72 1.54 1.3488 -2 6 1 4 69.77 2.59 1.3479 1 3 3 4 69.91 14.09 1.3456 5 3 1 4 70.93 3.77 1.3286 2 2 3 4 71.02 3.76 1.3273 -5 3 3 4 71.03 9.39 1.3271 -7 1 2 4 72.58 1.16 1.3026 -6 2 3 4 72.86 4.40 1.2982 -3 1 4 4 73.64 4.10 1.2864 -4 0 4 2 74.93 2.78 1.2674 7 1 0 4 75.91 1.99 1.2534 6 2 1 4 76.28 1.52 1.2483 -6 4 2 4 77.14 8.25 1.2365 0 6 2 4 77.23 2.17 1.2353 0 0 4 2 79.58 1.28 1.2046 4 6 0 4 80.68 1.76 1.1909 -1 7 1 4 80.71 1.02 1.1906 4 4 2 4 81.01 6.34 1.1869 3 5 2 4 82.25 2.33 1.1721 -6 0 4 2 82.26 1.12 1.1720 -4 6 2 4 82.83 2.01 1.1654 1 7 1 4 84.88 1.18 1.1424 2 6 2 4 88.70 1.23 1.1029 -4 4 4 4 89.95 2.44 1.0907 -7 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.