LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 343 K _database_code_amcsd 0007313 CELL PARAMETERS: 9.5633 8.5715 5.2686 90.000 110.223 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 405.253 Density (g/cm3): 3.750 MAX. ABS. INTENSITY / VOLUME**2: 21.16861163 RIR: 1.838 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.29 81.44 6.1983 1 1 0 4 19.79 3.65 4.4869 2 0 0 2 20.12 43.25 4.4125 -1 1 1 4 20.73 30.28 4.2857 0 2 0 2 25.59 37.57 3.4810 1 1 1 4 30.16 100.00 2.9635 -2 2 1 4 31.68 63.22 2.8242 3 1 0 4 32.90 8.76 2.7225 1 3 0 4 35.75 6.02 2.5116 -1 1 2 4 35.95 19.90 2.4981 -1 3 1 4 36.34 33.28 2.4719 0 0 2 2 37.76 27.77 2.3823 2 2 1 4 39.42 3.35 2.2857 1 3 1 4 39.86 2.88 2.2615 -3 1 2 4 40.90 2.87 2.2063 -2 2 2 4 42.17 2.55 2.1429 0 4 0 2 42.48 19.85 2.1279 1 1 2 4 43.24 18.86 2.0923 -3 3 1 4 43.57 10.09 2.0774 -4 2 1 4 44.15 8.93 2.0512 -4 0 2 2 46.17 1.28 1.9661 0 4 1 4 46.99 2.03 1.9337 2 4 0 4 47.75 4.57 1.9046 2 0 2 2 47.89 14.98 1.8994 -2 4 1 4 48.79 8.14 1.8664 -5 1 1 4 49.25 3.45 1.8502 -4 2 2 4 50.35 2.93 1.8124 -3 3 2 4 51.88 1.97 1.7625 3 3 1 4 52.73 1.03 1.7358 -5 1 2 4 53.39 3.61 1.7162 2 4 1 4 54.06 1.47 1.6964 -1 1 3 4 54.49 8.29 1.6838 1 5 0 4 54.80 4.18 1.6751 4 2 1 4 56.65 17.35 1.6247 -2 2 3 4 56.86 9.10 1.6192 0 4 2 4 56.95 9.60 1.6168 3 1 2 4 57.96 2.29 1.5910 -4 4 1 4 58.04 17.49 1.5892 -5 3 1 4 59.67 8.09 1.5496 4 4 0 4 60.24 3.88 1.5363 -6 0 2 2 61.07 1.04 1.5173 -4 2 3 4 61.59 3.49 1.5058 1 1 3 4 61.73 2.58 1.5026 5 1 1 4 62.05 3.55 1.4956 6 0 0 2 62.20 2.57 1.4925 -6 2 1 4 62.44 5.41 1.4874 3 5 0 4 62.70 2.68 1.4818 -4 4 2 4 62.77 9.18 1.4802 -1 3 3 4 62.94 3.84 1.4768 -5 1 3 4 63.22 3.24 1.4708 -3 3 3 4 64.96 1.90 1.4356 -1 5 2 4 65.09 2.87 1.4329 4 0 2 2 65.32 5.87 1.4286 0 6 0 2 67.53 1.21 1.3871 4 4 1 4 67.71 7.79 1.3838 -3 5 2 4 69.12 2.20 1.3590 4 2 2 4 69.17 5.80 1.3581 -2 4 3 4 69.70 1.54 1.3491 -2 6 1 4 69.73 2.58 1.3485 1 3 3 4 69.87 13.90 1.3462 5 3 1 4 70.89 3.73 1.3294 2 2 3 4 71.00 3.71 1.3275 -5 3 3 4 71.01 9.28 1.3274 -7 1 2 4 72.56 1.15 1.3028 -6 2 3 4 72.83 4.36 1.2986 -3 1 4 4 73.62 4.05 1.2867 -4 0 4 2 74.90 2.75 1.2679 7 1 0 4 75.87 1.97 1.2540 6 2 1 4 76.26 1.51 1.2486 -6 4 2 4 77.11 8.12 1.2369 0 6 2 4 77.18 2.15 1.2360 0 0 4 2 79.55 1.26 1.2050 4 6 0 4 80.65 1.74 1.1913 -1 7 1 4 80.66 1.01 1.1912 4 4 2 4 80.97 6.30 1.1875 3 5 2 4 82.24 1.10 1.1723 -4 6 2 4 82.24 2.28 1.1723 -6 0 4 2 82.80 2.00 1.1658 1 7 1 4 84.84 1.14 1.1428 2 6 2 4 88.67 1.23 1.1031 -4 4 4 4 89.94 2.40 1.0908 -7 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.