LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 383 K _database_code_amcsd 0007315 CELL PARAMETERS: 9.5666 8.5753 5.2691 90.000 110.219 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 405.622 Density (g/cm3): 3.747 MAX. ABS. INTENSITY / VOLUME**2: 21.11618686 RIR: 1.835 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.28 81.42 6.2008 1 1 0 4 19.78 3.64 4.4885 2 0 0 2 20.12 43.25 4.4134 -1 1 1 4 20.72 30.17 4.2877 0 2 0 2 25.58 37.51 3.4819 1 1 1 4 30.15 100.00 2.9645 -2 2 1 4 31.67 62.83 2.8253 3 1 0 4 32.88 8.85 2.7237 1 3 0 4 35.74 5.93 2.5120 -1 1 2 4 35.94 19.71 2.4990 -1 3 1 4 36.34 33.26 2.4722 0 0 2 2 37.75 27.68 2.3831 2 2 1 4 39.41 3.33 2.2865 1 3 1 4 39.85 2.91 2.2619 -3 1 2 4 40.90 2.83 2.2067 -2 2 2 4 42.15 2.58 2.1438 0 4 0 2 42.47 19.79 2.1283 1 1 2 4 43.22 18.65 2.0931 -3 3 1 4 43.55 9.98 2.0782 -4 2 1 4 44.14 8.82 2.0516 -4 0 2 2 46.15 1.29 1.9669 0 4 1 4 46.97 2.01 1.9345 2 4 0 4 47.74 4.49 1.9050 2 0 2 2 47.87 14.95 1.9001 -2 4 1 4 48.77 8.08 1.8671 -5 1 1 4 49.24 3.42 1.8507 -4 2 2 4 50.33 2.89 1.8129 -3 3 2 4 51.86 1.96 1.7631 3 3 1 4 52.72 1.00 1.7363 -5 1 2 4 53.36 3.56 1.7168 2 4 1 4 54.05 1.49 1.6965 -1 1 3 4 54.47 8.17 1.6846 1 5 0 4 54.78 4.12 1.6757 4 2 1 4 56.65 17.13 1.6249 -2 2 3 4 56.85 9.03 1.6197 0 4 2 4 56.94 9.49 1.6173 3 1 2 4 57.94 2.23 1.5916 -4 4 1 4 58.01 17.37 1.5898 -5 3 1 4 59.64 7.98 1.5502 4 4 0 4 60.22 3.84 1.5367 -6 0 2 2 61.06 1.03 1.5176 -4 2 3 4 61.58 3.42 1.5061 1 1 3 4 61.71 2.55 1.5031 5 1 1 4 62.03 3.48 1.4962 6 0 0 2 62.17 2.52 1.4931 -6 2 1 4 62.41 5.35 1.4880 3 5 0 4 62.68 2.66 1.4822 -4 4 2 4 62.76 9.10 1.4805 -1 3 3 4 62.92 3.79 1.4770 -5 1 3 4 63.21 3.15 1.4711 -3 3 3 4 64.93 1.85 1.4361 -1 5 2 4 65.07 2.82 1.4333 4 0 2 2 65.29 5.80 1.4292 0 6 0 2 67.50 1.18 1.3877 4 4 1 4 67.68 7.65 1.3843 -3 5 2 4 69.10 2.14 1.3594 4 2 2 4 69.15 5.70 1.3584 -2 4 3 4 69.67 1.51 1.3497 -2 6 1 4 69.72 2.50 1.3488 1 3 3 4 69.84 13.67 1.3467 5 3 1 4 70.87 3.69 1.3297 2 2 3 4 70.98 3.66 1.3278 -5 3 3 4 70.99 9.12 1.3278 -7 1 2 4 72.54 1.11 1.3031 -6 2 3 4 72.83 4.28 1.2987 -3 1 4 4 73.61 3.95 1.2869 -4 0 4 2 74.86 2.74 1.2683 7 1 0 4 75.84 1.94 1.2545 6 2 1 4 76.23 1.49 1.2490 -6 4 2 4 77.08 7.94 1.2373 0 6 2 4 77.17 2.11 1.2361 0 0 4 2 79.51 1.22 1.2055 4 6 0 4 80.61 1.73 1.1918 -1 7 1 4 80.63 1.01 1.1916 4 4 2 4 80.93 6.13 1.1879 3 5 2 4 82.20 1.08 1.1727 -4 6 2 4 82.22 2.22 1.1725 -6 0 4 2 82.76 1.93 1.1662 1 7 1 4 84.80 1.09 1.1432 2 6 2 4 88.65 1.21 1.1034 -4 4 4 4 89.92 2.35 1.0910 -7 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.