CaFe3Ti4O12 Leinenweber K, Linton J, Navrotsky A, Fei Y, Parise J B Physics and Chemistry of Minerals 22 (1995) 251-258 High-pressure perovskites on the join CaTiO3-FeTiO3 _database_code_amcsd 0007916 CELL PARAMETERS: 7.4672 7.4672 7.4672 90.000 90.000 90.000 SPACE GROUP: Im3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 416.361 Density (g/cm3): 4.714 MAX. ABS. INTENSITY / VOLUME**2: 77.41692653 RIR: 5.347 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 16.79 2.03 5.2801 1 1 0 12 29.30 2.56 3.0485 2 1 1 24 33.96 100.00 2.6400 2 2 0 12 38.11 3.67 2.3613 3 0 1 12 38.11 3.61 2.3613 3 1 0 12 41.91 5.48 2.1556 2 2 2 8 45.45 2.06 1.9957 3 2 1 24 45.45 2.37 1.9957 3 1 2 24 48.78 30.84 1.8668 4 0 0 6 51.95 1.06 1.7600 3 3 0 12 60.77 43.97 1.5242 4 2 2 24 71.47 11.68 1.3200 4 4 0 12 81.53 6.42 1.1807 6 2 0 12 81.53 5.48 1.1807 6 0 2 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.