Franklinite Levy D, Pavese A, Hanfland M Physics and Chemistry of Minerals 27 (2000) 638-644 Phase transition of synthetic zinc ferrite spinel (ZnFe2O4) at high pressure, from synchrotron X-ray powder diffraction Sample: P = 1.8 GPa _database_code_amcsd 0008476 CELL PARAMETERS: 8.4129 8.4129 8.4129 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 595.439 Density (g/cm3): 5.378 MAX. ABS. INTENSITY / VOLUME**2: 104.6094830 RIR: 6.333 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.26 4.26 4.8572 1 1 1 8 30.04 35.65 2.9744 2 2 0 12 35.39 100.00 2.5366 3 1 1 24 37.02 7.48 2.4286 2 2 2 8 43.00 13.38 2.1032 4 0 0 6 53.35 12.01 1.7173 4 2 2 24 56.87 27.30 1.6191 5 1 1 24 56.87 5.72 1.6191 3 3 3 8 62.45 38.37 1.4872 4 4 0 12 70.84 4.30 1.3302 6 2 0 24 73.87 8.72 1.2830 5 3 3 24 74.87 3.58 1.2683 6 2 2 24 78.82 1.48 1.2143 4 4 4 8 86.59 4.99 1.1242 6 4 2 48 89.48 7.88 1.0953 7 3 1 48 89.48 5.65 1.0953 5 5 3 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.