Rh6 Sn17.6 Tb5 Miraglia S, Hodeau J, de Bergevin F, Marezio M Acta Crystallographica B43 (1987) 76-83 Structural studies by electron and X-ray diffraction of the disordered phases II: (Sn1-xTbx)Tb4Rh6Sn18 and (Sn1-xDyX)Dy4Os6Sn18 _cod_database_code 1008324 _database_code_amcsd 0016239 CELL PARAMETERS: 13.7720 13.7720 27.5440 90.000 90.000 90.000 SPACE GROUP: I4_1/acd X-RAY WAVELENGTH: 1.541838 Cell Volume: 5224.215 Density (g/cm3): 8.902 MAX. ABS. INTENSITY / VOLUME**2: 281.3430604 RIR: 10.291 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.86 2.08 6.8860 0 0 4 2 12.86 4.64 6.8860 2 0 0 4 17.34 3.14 5.1148 2 1 3 16 18.22 1.90 4.8691 2 0 4 8 18.22 1.24 4.8691 2 2 0 4 21.64 4.66 4.1060 2 1 5 16 28.43 1.33 3.1389 4 1 3 16 31.32 2.72 2.8562 4 1 5 16 31.83 2.47 2.8112 2 2 8 8 31.83 3.82 2.8112 4 2 4 16 32.67 4.53 2.7407 3 2 7 16 32.67 4.59 2.7407 2 1 9 16 33.82 26.35 2.6504 5 1 2 16 33.82 60.18 2.6504 3 3 6 8 33.82 13.48 2.6504 1 1 10 8 33.98 3.58 2.6382 4 3 3 16 35.24 2.97 2.5464 5 2 1 16 35.24 1.84 2.5464 4 1 7 16 36.47 4.71 2.4636 5 2 3 16 36.47 2.53 2.4636 4 3 5 16 36.92 23.42 2.4346 4 0 8 8 36.92 11.20 2.4346 4 4 0 4 37.66 1.83 2.3884 3 2 9 16 38.68 3.73 2.3279 3 1 10 16 38.68 3.32 2.3279 5 3 2 16 38.68 3.65 2.3279 5 1 6 16 38.82 2.61 2.3196 2 1 11 16 38.82 3.15 2.3196 5 2 5 16 39.25 4.68 2.2953 0 0 12 2 39.25 10.44 2.2953 6 0 0 4 39.25 2.48 2.2953 4 4 4 8 39.25 4.12 2.2953 4 2 8 16 39.95 2.42 2.2565 6 1 1 16 41.06 2.10 2.1983 6 1 3 16 43.59 8.67 2.0762 2 2 12 8 43.59 14.36 2.0762 6 2 4 16 47.13 1.51 1.9285 7 1 2 16 47.61 1.14 1.9098 6 0 8 8 47.61 1.35 1.9098 6 4 0 8 51.05 1.29 1.7892 5 2 11 16 53.21 1.38 1.7215 8 0 0 4 53.21 1.04 1.7215 0 0 16 2 54.65 1.25 1.6794 6 5 5 16 54.65 1.04 1.6794 6 1 11 16 56.72 1.40 1.6230 2 2 16 8 56.72 11.22 1.6230 6 0 12 8 56.72 4.85 1.6230 6 6 0 4 56.72 1.63 1.6230 8 2 4 16 58.00 3.60 1.5903 5 5 10 8 59.78 1.40 1.5470 8 3 5 16 61.73 3.57 1.5026 8 4 4 16 61.73 3.33 1.5026 8 2 8 16 61.73 2.64 1.5026 4 2 16 16 62.24 1.64 1.4916 3 2 17 16 63.05 1.23 1.4744 9 2 3 16 64.65 2.91 1.4417 9 2 5 16 66.52 6.98 1.4056 8 4 8 16 66.52 4.13 1.4056 4 4 16 8 67.69 3.12 1.3841 3 3 18 8 67.69 5.71 1.3841 9 3 6 16 67.69 1.45 1.3841 7 5 10 16 70.77 1.04 1.3314 7 3 14 16 76.75 1.36 1.2418 7 5 14 16 80.05 1.84 1.1987 8 2 16 16 80.05 1.13 1.1987 8 8 4 8 82.96 1.41 1.1639 6 2 20 16 82.96 1.05 1.1639 10 2 12 16 84.40 1.56 1.1477 12 0 0 4 84.40 1.05 1.1477 0 0 24 2 84.40 1.13 1.1477 8 4 16 16 85.48 1.57 1.1359 5 1 22 16 85.48 1.42 1.1359 11 5 2 16 85.48 1.45 1.1359 11 1 10 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.