Rinneite Figgis B N, Sobolev A N, Kucharski E S, Broughton V Acta Crystallographica C56 (2000) e228-e229 Rinneite, K3Na[FeCl6], at 293, 84 and 9.5 K Locality: synthetic Sample: T = 9.5 K _database_code_amcsd 0010321 CELL PARAMETERS: 11.8930 11.8930 13.7350 90.000 90.000 120.000 SPACE GROUP: R-3c X-RAY WAVELENGTH: 1.541838 Cell Volume: 1682.450 Density (g/cm3): 2.421 MAX. ABS. INTENSITY / VOLUME**2: 16.14028988 RIR: 2.171 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.90 32.37 5.9465 1 1 0 6 15.51 51.66 5.7138 0 1 2 6 21.57 2.93 4.1201 2 0 2 6 23.76 4.79 3.7454 2 1 1 12 24.54 11.06 3.6277 1 1 3 12 25.95 24.78 3.4332 3 0 0 6 27.38 8.31 3.2575 1 0 4 6 30.06 4.71 2.9732 2 2 0 6 31.31 18.94 2.8569 0 2 4 6 32.00 61.01 2.7968 1 3 1 12 33.99 30.82 2.6375 3 1 2 12 34.84 56.05 2.5751 2 1 4 12 36.02 100.00 2.4936 2 2 3 12 38.67 4.85 2.3287 3 2 1 12 39.36 10.84 2.2892 0 0 6 2 40.12 7.88 2.2476 4 1 0 12 40.18 7.56 2.2445 1 2 5 12 40.37 3.03 2.2343 2 3 2 12 41.10 8.64 2.1960 1 3 4 12 42.31 6.14 2.1363 1 1 6 12 43.95 3.43 2.0600 4 0 4 6 44.93 1.15 2.0176 1 4 3 12 45.78 5.04 1.9822 3 3 0 6 45.83 2.76 1.9800 3 1 5 12 46.66 31.28 1.9465 3 2 4 12 47.75 1.88 1.9046 3 0 6 6 48.62 3.11 1.8727 4 2 2 12 49.73 8.47 1.8333 5 1 1 12 50.30 11.00 1.8138 2 2 6 12 50.98 1.12 1.7914 2 3 5 12 51.14 3.68 1.7862 1 5 2 12 51.75 1.68 1.7664 0 5 4 6 52.21 2.82 1.7522 2 1 7 12 53.37 19.90 1.7166 6 0 0 6 54.16 6.64 1.6935 0 1 8 6 55.74 7.77 1.6493 5 2 0 12 55.93 4.56 1.6440 3 4 2 12 56.50 2.08 1.6287 2 0 8 6 56.93 11.61 1.6174 1 3 7 12 57.46 2.76 1.6038 1 4 6 12 58.78 1.50 1.5709 1 2 8 12 59.21 7.27 1.5605 1 6 1 12 59.58 2.12 1.5517 2 5 3 12 60.32 4.50 1.5344 1 5 5 12 60.46 2.65 1.5311 6 1 2 12 61.01 1.23 1.5186 4 3 4 12 61.42 4.77 1.5095 3 2 7 12 62.87 2.10 1.4782 1 1 9 12 64.80 6.12 1.4387 5 3 2 12 65.32 1.07 1.4285 0 4 8 6 65.73 1.78 1.4206 6 2 1 12 66.08 2.53 1.4140 4 4 3 12 66.91 1.25 1.3984 2 6 2 12 67.43 3.41 1.3889 2 3 8 12 67.82 1.97 1.3819 2 4 7 12 68.30 1.05 1.3734 0 6 6 6 68.82 1.15 1.3642 7 1 0 12 68.86 7.08 1.3635 6 1 5 12 68.98 3.45 1.3614 1 0 10 6 69.20 2.37 1.3577 2 2 9 12 69.50 13.96 1.3524 3 5 4 12 71.54 5.46 1.3189 5 0 8 6 71.55 1.64 1.3188 6 2 4 12 71.93 1.15 1.3127 5 4 1 12 72.94 1.12 1.2970 5 3 5 12 73.06 2.63 1.2951 4 5 2 12 75.27 1.61 1.2626 1 4 9 12 75.56 3.50 1.2584 1 5 8 12 76.39 2.25 1.2468 4 4 6 12 79.51 2.54 1.2055 0 8 4 6 80.84 2.91 1.1890 1 2 11 12 81.46 1.04 1.1815 2 7 4 12 81.82 1.25 1.1772 3 5 7 12 83.40 1.60 1.1589 6 1 8 12 84.74 1.10 1.1440 7 2 5 12 85.34 3.66 1.1374 8 1 4 12 86.14 3.11 1.1289 6 3 6 12 86.78 1.22 1.1222 2 4 10 12 86.98 1.91 1.1201 5 2 9 12 87.26 1.17 1.1172 0 7 8 6 87.26 4.91 1.1172 5 3 8 12 88.58 1.02 1.1040 2 3 11 12 88.71 1.95 1.1028 5 1 10 12 89.55 1.00 1.0945 5 4 7 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.