Moissanite 6H Ott H Zeitschrift fur Kristallographie 61 (1925) 515-531 Die Gitterstruktur des Karborunds ( Si C ) I. _cod_database_code 1011053 _database_code_amcsd 0017954 CELL PARAMETERS: 3.0950 3.0950 15.1700 90.000 90.000 120.000 SPACE GROUP: P6_3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 125.845 Density (g/cm3): 3.174 MAX. ABS. INTENSITY / VOLUME**2: 13.22671447 RIR: 1.357 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 33.96 56.13 2.6395 1 0 1 6 35.51 66.75 2.5283 0 0 6 1 35.52 100.00 2.5272 1 0 2 6 37.99 58.99 2.3682 1 0 3 6 41.24 23.38 2.1889 1 0 4 6 45.14 8.96 2.0087 1 0 5 6 54.45 11.82 1.6852 1 0 7 6 59.74 29.10 1.5480 1 0 8 6 59.76 58.03 1.5475 1 1 0 6 65.41 25.63 1.4269 1 0 9 6 70.55 5.01 1.3350 2 0 1 6 71.46 10.51 1.3202 1 0 10 6 71.48 42.10 1.3199 1 1 6 6 71.49 10.52 1.3197 2 0 2 6 73.04 8.29 1.2954 2 0 3 6 75.15 2.89 1.2642 0 0 12 1 75.19 4.33 1.2636 2 0 4 6 77.90 1.73 1.2263 1 0 11 6 77.93 1.72 1.2259 2 0 5 6 85.12 2.89 1.1398 2 0 7 6 89.56 8.61 1.0944 2 0 8 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.