Retgersite Beevers C A, Lipson H Zeitschrift fur Kristallographie 83 (1932) 123-135 The crystal structure of nickel sulphate hexahydrate NiSO4 * 6H2O Locality: synthetic _database_code_amcsd 0010508 CELL PARAMETERS: 6.8000 6.8000 18.3000 90.000 90.000 90.000 SPACE GROUP: P4_12_12 X-RAY WAVELENGTH: 1.541838 Cell Volume: 846.192 Density (g/cm3): 2.165 MAX. ABS. INTENSITY / VOLUME**2: 23.04489886 RIR: 3.466 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.89 15.16 6.3742 1 0 1 8 16.24 1.11 5.4578 1 0 2 8 19.08 6.66 4.6505 1 1 1 8 19.40 35.88 4.5750 0 0 4 2 19.55 2.42 4.5407 1 0 3 8 20.87 100.00 4.2564 1 1 2 8 23.56 5.43 3.7762 1 1 3 8 26.21 7.96 3.4000 2 0 0 4 26.67 3.72 3.3428 2 0 1 8 28.00 2.12 3.1871 2 0 2 8 29.37 1.84 3.0411 2 1 0 8 30.09 17.08 2.9698 2 0 3 8 30.70 2.70 2.9123 1 1 5 8 30.99 2.07 2.8858 2 1 2 8 32.16 1.28 2.7829 1 0 6 8 32.82 15.53 2.7289 2 0 4 8 34.83 10.88 2.5756 1 1 6 8 35.44 8.32 2.5326 2 1 4 8 38.49 15.40 2.3390 2 1 5 8 41.66 1.31 2.1681 1 0 8 8 42.32 7.17 2.1357 3 1 1 8 42.48 2.62 2.1282 2 2 4 8 42.55 5.54 2.1247 3 0 3 8 43.22 5.17 2.0933 3 1 2 8 44.61 2.97 2.0311 3 0 4 8 44.68 3.42 2.0280 3 1 3 8 45.12 1.33 2.0094 2 2 5 8 45.77 4.69 1.9824 2 1 7 8 46.67 2.47 1.9461 3 1 4 8 47.93 5.97 1.8979 2 0 8 8 48.25 2.64 1.8860 3 2 0 8 49.14 5.74 1.8540 3 1 5 8 49.34 1.41 1.8472 3 2 2 8 49.89 4.04 1.8281 2 1 8 8 52.04 7.43 1.7575 3 1 6 8 53.58 4.31 1.7103 1 1 10 8 54.19 3.55 1.6927 4 0 1 8 54.27 1.74 1.6903 2 1 9 8 55.32 1.79 1.6607 3 1 7 8 55.44 5.49 1.6572 2 2 8 8 55.98 2.29 1.6426 4 1 1 8 56.17 3.03 1.6376 4 0 3 8 57.74 2.01 1.5967 3 3 1 8 57.86 1.19 1.5935 4 0 4 8 57.92 1.04 1.5921 4 1 3 8 60.00 2.02 1.5418 4 0 5 8 60.53 1.15 1.5295 3 2 7 8 60.73 1.02 1.5250 0 0 12 2 60.93 1.31 1.5205 4 2 0 8 61.16 2.13 1.5153 4 2 1 8 61.86 1.44 1.5000 4 2 2 8 62.91 1.78 1.4774 3 1 9 8 63.77 1.23 1.4595 2 1 11 8 65.49 1.29 1.4252 4 0 7 8 66.60 2.27 1.4042 4 2 5 8 67.17 1.44 1.3936 3 1 10 8 67.29 1.10 1.3914 2 0 12 8 67.77 1.60 1.3828 3 2 9 8 68.60 1.06 1.3680 2 2 11 8 70.85 1.20 1.3301 5 1 1 8 71.82 1.05 1.3144 4 2 7 8 72.56 1.65 1.3028 5 1 3 8 73.55 1.18 1.2878 2 2 12 8 75.35 1.85 1.2614 1 1 14 8 75.94 1.19 1.2530 5 1 5 8 80.61 1.53 1.1918 4 4 2 8 80.92 2.64 1.1880 5 1 7 8 87.47 1.80 1.1151 5 1 9 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.