Bi2.22 O4 Sr0.78 Sillen L, Aurivillius B Zeitschrift fur Kristallographie 101 (1939) 483-495 Oxide phases with a defect oxygen lattice _cod_database_code 1010022 _database_code_amcsd 0016961 CELL PARAMETERS: 3.9700 3.9700 28.5900 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 390.235 Density (g/cm3): 7.615 MAX. ABS. INTENSITY / VOLUME**2: 216.0569132 RIR: 9.239 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.28 8.98 9.5300 0 0 3 2 18.62 10.96 4.7650 0 0 6 2 26.10 19.61 3.4135 1 0 1 6 26.67 57.93 3.3428 0 1 2 6 28.09 54.95 3.1767 0 0 9 2 28.82 100.00 3.0983 1 0 4 6 30.33 73.21 2.9465 0 1 5 6 34.09 13.26 2.6303 1 0 7 6 36.26 18.98 2.4777 0 1 8 6 41.06 2.45 2.1983 1 0 10 6 43.66 21.66 2.0733 0 1 11 6 45.71 51.40 1.9850 1 1 0 6 46.75 1.16 1.9433 1 1 3 12 47.72 1.61 1.9060 0 0 15 2 49.18 29.55 1.8526 1 0 13 6 49.76 4.64 1.8324 1 1 6 12 52.09 10.98 1.7558 0 1 14 6 53.39 2.40 1.7160 0 2 1 6 53.70 7.36 1.7068 2 0 2 6 54.51 44.77 1.6834 1 1 9 12 54.93 14.65 1.6714 0 2 4 6 55.85 11.37 1.6463 2 0 5 6 58.07 4.25 1.5883 0 0 18 2 58.19 2.25 1.5855 1 0 16 6 58.23 2.80 1.5844 0 2 7 6 59.69 3.84 1.5492 2 0 8 6 61.37 6.83 1.5107 0 1 17 6 65.05 5.43 1.4338 2 0 11 6 68.21 2.95 1.3748 1 1 15 12 69.39 8.91 1.3544 0 2 13 6 71.47 2.83 1.3200 0 1 20 6 71.77 3.53 1.3151 2 0 14 6 72.86 1.62 1.2981 2 1 1 12 73.12 5.03 1.2942 1 2 2 12 74.17 10.38 1.2785 2 1 4 12 74.94 8.14 1.2672 1 2 5 12 76.87 9.82 1.2402 1 1 18 12 77.01 2.25 1.2383 2 1 7 12 78.28 2.98 1.2213 1 2 8 12 78.72 7.02 1.2156 1 0 22 6 79.77 2.71 1.2022 2 0 17 6 82.52 1.28 1.1690 0 1 23 6 83.10 4.63 1.1623 1 2 11 12 84.55 6.05 1.1460 3 0 0 6 87.11 8.46 1.1188 2 1 13 12 89.08 1.42 1.0991 2 0 20 6 89.36 3.51 1.0963 1 2 14 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.