Covellite Fjellvag H, Gronvold F, Stolen S, Andresen A F, Mueller-Kaefer R, Simon A Zeitschrift fur Kristallographie 184 (1988) 111-121 Low-temperature structural distortion in CuS Locality: synthetic Sample: T = 8 K Note: Cell parameters estimated from Figure 1 _database_code_amcsd 0010981 CELL PARAMETERS: 3.7630 6.5680 16.2250 90.000 90.000 90.000 SPACE GROUP: Cmcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 401.007 Density (g/cm3): 4.750 MAX. ABS. INTENSITY / VOLUME**2: 37.63480997 RIR: 2.580 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.91 9.97 8.1125 0 0 2 2 21.91 1.65 4.0563 0 0 4 2 27.15 2.37 3.2840 0 2 0 2 27.31 16.96 3.2651 1 1 0 4 27.72 4.08 3.2187 0 2 1 4 27.87 24.44 3.2009 1 1 1 8 29.34 18.61 3.0440 0 2 2 4 29.49 58.34 3.0290 1 1 2 8 31.88 75.53 2.8070 0 2 3 4 32.02 100.00 2.7952 1 1 3 8 33.13 76.83 2.7042 0 0 6 2 35.16 1.03 2.5524 0 2 4 4 39.02 9.71 2.3082 0 2 5 4 39.14 7.98 2.3016 1 1 5 8 43.34 1.11 2.0875 0 2 6 4 43.45 7.96 2.0826 1 1 6 8 44.68 8.79 2.0281 0 0 8 2 48.05 5.24 1.8937 0 2 7 4 48.08 75.65 1.8924 1 3 0 4 48.14 16.37 1.8900 1 1 7 8 48.38 40.86 1.8815 2 0 0 2 48.43 3.52 1.8796 1 3 1 8 51.14 5.57 1.7862 1 3 3 8 53.07 12.28 1.7256 0 2 8 4 53.16 34.98 1.7228 1 1 8 8 53.43 1.89 1.7149 1 3 4 8 56.00 1.77 1.6420 0 4 0 2 56.28 2.99 1.6347 1 3 5 8 56.32 3.47 1.6337 0 4 1 4 57.24 3.93 1.6094 0 4 2 4 57.59 4.18 1.6005 2 2 2 8 58.40 2.81 1.5803 0 2 9 4 58.48 2.50 1.5782 1 1 9 8 58.77 4.16 1.5712 0 4 3 4 59.11 23.35 1.5629 2 2 3 8 59.63 42.69 1.5504 1 3 6 8 59.89 23.86 1.5444 2 0 6 4 63.46 1.24 1.4659 1 3 7 8 63.82 4.06 1.4584 2 2 5 8 64.01 1.56 1.4546 0 2 10 4 64.09 1.99 1.4530 1 1 10 8 66.63 1.39 1.4035 0 4 6 4 67.72 6.97 1.3836 1 3 8 8 67.96 4.39 1.3793 2 0 8 4 69.91 6.62 1.3455 0 2 11 4 69.99 8.68 1.3442 1 1 11 8 70.25 3.84 1.3399 0 4 7 4 70.56 2.93 1.3347 2 2 7 8 72.40 1.36 1.3053 1 3 9 8 74.33 6.59 1.2762 0 4 8 4 74.63 8.14 1.2717 2 2 8 8 77.09 1.14 1.2371 2 4 0 4 77.36 2.48 1.2336 2 4 1 8 78.15 2.89 1.2230 2 4 2 8 78.53 2.66 1.2181 3 1 2 8 79.15 2.00 1.2101 2 2 9 8 79.25 10.26 1.2088 1 5 3 8 79.47 2.98 1.2060 2 4 3 8 79.84 5.75 1.2013 3 1 3 8 83.01 1.10 1.1634 1 3 11 8 83.40 2.84 1.1589 0 0 14 2 83.43 2.27 1.1585 1 5 5 8 84.12 1.35 1.1508 2 2 10 8 86.51 1.15 1.1250 2 4 6 8 89.27 1.00 1.0973 0 4 11 4 89.54 4.08 1.0947 0 6 0 2 89.56 6.30 1.0945 2 2 11 8 89.66 1.27 1.0935 1 5 7 8 89.72 2.75 1.0929 0 2 14 4 89.80 7.86 1.0922 1 1 14 8 89.88 3.83 1.0914 2 4 7 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.