Szomolnokite Le Fur Y, Coing-Boyat J, Bassi G Comptes Rendus de l'Academie des Sciences Paris C262 (1966) 632-635 Structure des sulfates monohydrates, monocliniques, des metaux de transition, MSO4*H2O (M = Mn, Fe, Co, Ni et Zn) Locality: synthetic _database_code_amcsd 0021021 CELL PARAMETERS: 7.0750 7.5410 7.6000 90.000 116.183 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 363.873 Density (g/cm3): 3.141 MAX. ABS. INTENSITY / VOLUME**2: 23.08295943 RIR: 2.393 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.27 16.47 4.8569 1 1 0 4 18.51 7.96 4.7940 -1 1 1 4 23.60 43.98 3.7705 0 2 0 2 25.86 8.10 3.4448 1 1 1 4 26.38 100.00 3.3782 -1 1 2 4 27.02 34.16 3.2998 0 2 1 4 28.11 64.24 3.1745 2 0 0 2 34.78 17.50 2.5793 -2 2 1 4 35.49 3.23 2.5291 0 2 2 4 36.97 6.93 2.4315 1 1 2 4 37.02 2.64 2.4284 2 2 0 4 37.52 1.17 2.3970 -2 2 2 4 37.60 2.90 2.3922 -1 1 3 4 38.52 16.90 2.3372 1 3 0 4 40.81 5.12 2.2110 -3 1 2 4 43.23 25.73 2.0929 -1 3 2 4 43.58 11.69 2.0769 2 2 1 4 44.45 2.03 2.0379 -2 2 3 4 44.46 10.30 2.0376 3 1 0 4 45.43 1.07 1.9963 -3 1 3 4 46.65 2.78 1.9469 0 2 3 4 46.93 1.03 1.9362 2 0 2 2 48.17 13.59 1.8893 -2 0 4 2 48.27 2.43 1.8852 0 4 0 2 50.38 3.71 1.8112 -1 1 4 4 50.82 3.13 1.7966 1 3 2 4 51.70 1.88 1.7681 -4 0 2 2 53.18 5.40 1.7224 2 2 2 4 53.45 2.07 1.7143 -3 1 4 4 53.76 2.91 1.7050 0 0 4 2 53.87 4.03 1.7019 -3 3 2 4 54.31 15.21 1.6891 -2 2 4 4 55.71 10.72 1.6499 0 4 2 4 56.87 9.47 1.6190 3 3 0 4 57.16 9.62 1.6115 -2 4 2 4 57.58 2.69 1.6008 -4 2 2 4 58.12 9.00 1.5873 4 0 0 2 58.94 2.53 1.5670 -4 2 1 4 59.50 4.16 1.5536 0 2 4 4 59.54 3.14 1.5526 -4 0 4 2 59.65 1.44 1.5501 -4 2 3 4 61.94 1.21 1.4982 -1 3 4 4 62.22 4.55 1.4922 3 1 2 4 62.42 1.24 1.4877 -2 4 3 4 63.39 1.32 1.4674 1 5 0 4 63.60 2.66 1.4629 4 2 0 4 63.65 3.70 1.4619 1 1 4 4 64.18 1.79 1.4512 0 4 3 4 64.96 2.80 1.4357 -4 2 4 4 66.31 1.46 1.4097 -2 2 5 4 66.78 1.86 1.4007 -1 5 2 4 67.55 2.75 1.3868 -5 1 2 4 69.60 7.36 1.3507 2 4 2 4 71.21 1.48 1.3242 4 2 1 4 71.49 2.28 1.3197 -5 1 4 4 72.61 1.97 1.3021 3 3 2 4 73.13 1.32 1.2941 -4 2 5 4 73.42 6.81 1.2897 -4 4 2 4 73.78 2.06 1.2843 2 0 4 2 73.89 1.20 1.2827 0 2 5 4 73.94 1.58 1.2819 1 3 4 4 75.26 1.19 1.2627 -4 4 3 4 76.71 3.80 1.2423 -3 1 6 4 77.60 2.13 1.2303 -5 3 2 4 77.76 1.97 1.2282 3 5 0 4 78.71 3.23 1.2157 2 2 4 4 79.92 1.22 1.2003 -1 1 6 4 80.26 1.11 1.1961 -2 2 6 4 81.35 1.71 1.1828 -5 3 4 4 81.64 2.77 1.1793 0 6 2 4 82.18 2.31 1.1729 -1 5 4 4 82.86 2.58 1.1650 -2 6 2 4 84.61 1.75 1.1453 -3 5 4 4 86.41 1.14 1.1261 -3 3 6 4 87.21 1.22 1.1178 -5 1 6 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.