CdCr2Se4 Raccah P M, Bouchard R J, Wold A Journal of Applied Physics 37 (1966) 1436-1437 Locality: synthetic Crystallographic study of chromium spinels _database_code_amcsd 0012913 CELL PARAMETERS: 10.7400 10.7400 10.7400 90.000 90.000 90.000 SPACE GROUP: Fd-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1238.833 Density (g/cm3): 5.707 MAX. ABS. INTENSITY / VOLUME**2: 102.7781345 RIR: 5.864 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.28 2.32 6.2007 1 1 1 8 23.43 47.25 3.7972 2 2 0 12 27.55 58.24 3.2382 3 1 1 24 28.80 45.32 3.1004 2 2 2 8 33.37 51.51 2.6850 4 0 0 6 36.47 16.34 2.4639 3 3 1 24 41.18 13.79 2.1923 4 2 2 24 43.80 55.96 2.0669 5 1 1 24 47.91 100.00 1.8986 4 4 0 12 51.02 1.03 1.7900 4 4 2 24 54.00 3.60 1.6981 6 2 0 24 56.16 7.56 1.6378 5 3 3 24 56.87 12.44 1.6191 6 2 2 24 59.64 8.62 1.5502 4 4 4 8 61.68 4.61 1.5039 5 5 1 24 61.68 3.45 1.5039 7 1 1 24 64.98 11.12 1.4352 6 4 2 48 66.92 11.40 1.3982 5 5 3 24 70.09 11.69 1.3425 8 0 0 6 71.97 7.68 1.3121 7 3 3 24 75.05 3.48 1.2657 6 6 0 12 75.05 2.45 1.2657 8 2 2 24 76.87 5.54 1.2401 5 5 5 8 76.87 3.59 1.2401 7 5 1 48 77.48 3.16 1.2320 6 6 2 24 79.89 7.37 1.2008 8 4 0 24 81.68 1.81 1.1789 9 1 1 24 81.68 1.63 1.1789 7 5 3 48 82.28 1.60 1.1718 8 4 2 48 86.43 11.28 1.1259 9 3 1 48 89.38 19.66 1.0961 8 4 4 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.