Nahcolite Zachariasen W Journal of Chemical Physics 1 (1933) 634-639 The Crystal Lattice of Sodium Bicarbonate, Na H C O3 _cod_database_code 1011016 _database_code_amcsd 0017923 CELL PARAMETERS: 7.5100 9.7000 3.5300 90.000 93.320 90.000 SPACE GROUP: P2_1/n X-RAY WAVELENGTH: 1.541838 Cell Volume: 256.718 Density (g/cm3): 2.173 MAX. ABS. INTENSITY / VOLUME**2: 4.938659163 RIR: 0.740 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.93 4.17 5.9320 1 1 0 4 18.29 14.54 4.8500 0 2 0 2 23.74 2.22 3.7487 2 0 0 2 25.47 26.16 3.4967 2 1 0 4 26.92 3.83 3.3123 0 1 1 4 27.33 18.54 3.2629 -1 0 1 2 28.61 22.00 3.1205 1 0 1 2 28.87 30.64 3.0926 -1 1 1 4 30.08 89.90 2.9706 1 1 1 4 30.10 15.60 2.9690 1 3 0 4 30.13 54.50 2.9660 2 2 0 4 31.38 1.13 2.8509 0 2 1 4 33.09 23.90 2.7073 -1 2 1 4 34.17 100.00 2.6243 1 2 1 4 37.15 1.34 2.4201 3 1 0 4 38.78 30.78 2.3223 -2 2 1 4 39.04 2.15 2.3073 1 4 0 4 40.61 30.40 2.2215 3 2 0 4 43.15 1.90 2.0967 -3 0 1 2 44.24 17.00 2.0474 -2 3 1 4 44.50 13.44 2.0361 2 4 0 4 45.40 5.69 1.9977 0 4 1 4 45.71 17.86 1.9850 3 0 1 2 45.89 7.55 1.9773 3 3 0 4 45.93 1.29 1.9760 2 3 1 4 46.67 7.76 1.9463 -1 4 1 4 47.23 6.12 1.9245 -3 2 1 4 47.48 21.61 1.9148 1 4 1 4 48.47 4.26 1.8781 1 5 0 4 48.57 2.62 1.8743 4 0 0 2 49.62 2.60 1.8371 3 2 1 4 51.10 3.93 1.7875 -2 4 1 4 51.89 7.01 1.7620 0 0 2 2 52.33 3.24 1.7483 4 2 0 4 52.59 4.10 1.7404 3 4 0 4 52.81 1.73 1.7337 0 1 2 4 53.57 11.65 1.7106 -1 1 2 4 53.95 2.21 1.6995 0 5 1 4 54.96 11.83 1.6707 -4 1 1 4 55.48 1.76 1.6561 0 2 2 4 55.80 2.85 1.6476 1 5 1 4 56.23 1.09 1.6360 -1 2 2 4 56.40 1.46 1.6314 -2 0 2 2 56.96 8.96 1.6167 0 6 0 2 57.83 5.28 1.5945 4 1 1 4 58.16 3.90 1.5860 -3 4 1 4 59.05 1.14 1.5644 -2 5 1 4 59.22 2.74 1.5603 2 0 2 2 60.06 13.31 1.5405 2 1 2 4 60.25 1.96 1.5360 3 4 1 4 60.36 1.81 1.5335 4 2 1 4 60.43 3.40 1.5319 2 5 1 4 60.48 1.22 1.5308 -1 3 2 4 62.54 2.25 1.4853 2 2 2 4 62.57 3.46 1.4845 2 6 0 4 62.64 1.43 1.4830 4 4 0 4 63.29 1.75 1.4694 0 6 1 4 64.31 2.20 1.4486 -1 6 1 4 64.44 1.21 1.4459 4 3 1 4 65.11 2.12 1.4326 5 2 0 4 65.48 1.29 1.4255 0 4 2 4 67.45 1.09 1.3885 1 4 2 4 69.04 3.69 1.3603 5 3 0 4 69.44 1.80 1.3535 -5 2 1 4 69.77 1.37 1.3480 4 5 0 4 69.85 5.99 1.3465 -3 3 2 4 71.96 1.37 1.3121 2 4 2 4 72.07 1.15 1.3105 -4 1 2 4 76.19 1.57 1.2496 6 0 0 2 78.06 1.17 1.2242 4 6 0 4 78.70 1.28 1.2158 2 5 2 4 79.25 1.94 1.2089 4 2 2 4 80.70 1.16 1.1907 -6 1 1 4 84.34 3.58 1.1483 -2 6 2 4 85.83 1.02 1.1321 -2 1 3 4 87.06 1.21 1.1193 1 2 3 4 87.56 2.17 1.1143 4 7 0 4 88.57 2.59 1.1041 0 3 3 4 89.93 1.05 1.0909 3 8 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.