Ba2 N2 Zn Yamane H, DiSalvo F Journal of Solid State Chemistry 119 (1995) 375-379 Synthesis and crystal structure of Sr2 Zn N2 and Ba2 Zn N2 _cod_database_code 1005020 _database_code_amcsd 0013875 CELL PARAMETERS: 4.1520 4.1520 13.0550 90.000 90.000 90.000 SPACE GROUP: I4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 225.057 Density (g/cm3): 5.431 MAX. ABS. INTENSITY / VOLUME**2: 195.2407441 RIR: 11.706 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.57 2.06 6.5275 0 0 2 2 22.47 6.86 3.9567 1 0 1 8 27.33 6.95 3.2638 0 0 4 2 29.74 100.00 3.0040 1 0 3 8 30.45 66.85 2.9359 1 1 0 4 41.37 8.23 2.1827 1 1 4 8 41.50 11.15 2.1758 0 0 6 2 43.60 23.14 2.0760 2 0 0 4 49.59 1.81 1.8383 2 1 1 16 52.22 3.81 1.7517 2 0 4 8 52.34 21.18 1.7481 1 1 6 8 53.67 35.56 1.7079 2 1 3 16 53.89 3.09 1.7013 1 0 7 8 61.76 12.09 1.5020 2 0 6 8 63.36 6.64 1.4680 2 2 0 4 68.52 6.53 1.3694 1 0 9 8 70.32 1.40 1.3388 2 2 4 8 71.54 6.94 1.3189 3 0 3 8 71.73 2.62 1.3159 2 1 7 16 71.91 8.65 1.3130 3 1 0 8 78.53 2.00 1.2181 3 1 4 16 78.62 5.46 1.2169 2 2 6 8 80.52 1.87 1.1929 1 1 10 8 84.82 6.81 1.1431 2 1 9 16 86.59 8.33 1.1242 3 1 6 16 87.66 7.75 1.1132 3 2 3 16 88.47 1.48 1.1051 2 0 10 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.