Magnesium Raynor G V, Hume-Rothery W Journal of the Institute of Metals 65 (1939) 477-485 A technique for the X-ray powder photography of reactive metals and alloys with special reference to the lattice spacing of magnesium at high temperatures Locality: synthetic Sample: at T = 27.7 C Note: experiment #6 _database_code_amcsd 0014115 CELL PARAMETERS: 3.2032 3.2032 5.2010 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 46.215 Density (g/cm3): 1.746 MAX. ABS. INTENSITY / VOLUME**2: 20.68368172 RIR: 3.857 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 32.27 24.18 2.7741 1 0 0 6 34.49 26.66 2.6005 0 0 2 2 36.72 100.00 2.4477 1 0 1 12 47.95 14.62 1.8972 1 0 2 12 57.55 15.71 1.6016 1 1 0 6 63.25 16.78 1.4702 1 0 3 12 67.53 2.20 1.3870 2 0 0 6 68.85 16.40 1.3637 1 1 2 12 70.23 11.44 1.3402 2 0 1 12 72.73 2.24 1.3003 0 0 4 2 78.09 2.61 1.2238 2 0 2 12 81.81 2.22 1.1773 1 0 4 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.