Anorthite Klein S, Korekawa M Neues Jahrbuch fur Mineralogie, Monatshefte 1976 (1976) 66-69 Die gemittelte Struktur des Labradorits _cod_database_code 1008757 _database_code_amcsd 0016634 8.176 12.841 14.207 93.53 116.27 89.77 C-1 atom x y z occ B(1,1) B(2,2) B(3,3) B(1,2) B(1,3) B(2,3) Na1 .2675 .9728 .0867 .48 .31 2.33 .83 -.49 .14 -.95 Na2 .2675 .9728 .5867 .48 .31 2.33 .83 -.49 .14 -.95 Ca1 .2696 .0268 .052 .52 1.26 2.57 2.24 .41 .21 -.78 Ca2 .2696 .0268 .552 .52 1.26 2.57 2.24 .41 .21 -.78 Si1 .6823 .8797 .1738 .625 .62 .59 .47 .05 .07 .17 Si2 .6823 .8797 .6738 .625 .62 .59 .47 .05 .07 .17 Al1 .6823 .8797 .1738 .375 .62 .59 .47 .05 .07 .17 Al2 .6823 .8797 .6738 .375 .62 .59 .47 .05 .07 .17 Si3 .6862 .1095 .1585 .625 .56 .48 .49 .18 .04 -.01 Si4 .6862 .1095 .6585 .625 .56 .48 .49 .18 .04 -.01 Al3 .6862 .1095 .1585 .375 .56 .48 .49 .18 .04 -.01 Al4 .6862 .1095 .6585 .375 .56 .48 .49 .18 .04 -.01 Si5 .0036 .8177 .1159 .625 .76 .93 .36 .5 .06 .07 Si6 .0036 .8177 .6159 .625 .76 .93 .36 .5 .06 .07 Al5 .0036 .8177 .1159 .375 .76 .93 .36 .5 .06 .07 Al6 .0036 .8177 .6159 .375 .76 .93 .36 .5 .06 .07 Si7 .006 .1647 .1069 .625 .82 1.11 .44 -.21 .11 .2 Si8 .006 .1647 .6069 .625 .82 1.11 .44 -.21 .11 .2 Al7 .006 .1647 .1069 .375 .82 1.11 .44 -.21 .11 .2 Al8 .006 .1647 .6069 .375 .82 1.11 .44 -.21 .11 .2 O1 .1884 .867 .2158 1.78 1.73 1.37 .26 .01 .12 O2 .1884 .867 .7158 1.78 1.73 1.37 .26 .01 .12 O3 .1987 .1077 .1918 1.68 1.72 1.03 -.01 .19 .18 O4 .1987 .1077 .6918 1.68 1.72 1.03 -.01 .19 .18 O5 .0149 .6888 .1085 2.02 2.2 1.55 1.09 .07 -.4 O6 .0149 .6888 .6085 2.02 2.2 1.55 1.09 .07 -.4 O7 .014 .2919 .139 1.81 1.93 1.54 -.2 .58 .33 O8 .014 .2919 .639 1.81 1.93 1.54 -.2 .58 .33 O9 .3111 .3537 .1232 1.94 1.64 3.12 .2 1.23 -.19 O10 .3111 .3537 .6232 1.94 1.64 3.12 .2 1.23 -.19 O11 .3121 .6066 .0949 1.63 1.45 1.78 -.07 .69 -.01 O12 .3121 .6066 .5949 1.63 1.45 1.78 -.07 .69 -.01 O13 .0821 .4936 .139 1.11 1.06 1.14 .03 .29 .23 O14 .0821 .4936 .639 1.11 1.06 1.14 .03 .29 .23 O15 .0037 .1297 .9896 2.33 2.46 .96 .22 .74 .4 O16 .0037 .1297 .4896 2.33 2.46 .96 .22 .74 .4