Wurtzite-2H Ballentyne D W G, Roy B Physica 27 (1961) 337-341 Electroluminescence and crystal structure in the alloy system ZnS - CdS Locality: synthetic _database_code_amcsd 0014998 CELL PARAMETERS: 3.8180 3.8180 6.2600 90.000 90.000 120.000 SPACE GROUP: P6_3mc X-RAY WAVELENGTH: 1.541838 Cell Volume: 79.027 Density (g/cm3): 4.096 MAX. ABS. INTENSITY / VOLUME**2: 50.51954304 RIR: 4.016 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 26.97 92.64 3.3065 1 0 0 6 28.52 59.52 3.1300 0 0 2 1 30.58 100.00 2.9237 1 0 1 6 39.65 34.34 2.2731 1 0 2 6 47.64 66.62 1.9090 1 1 0 6 51.81 65.88 1.7646 1 0 3 6 55.59 9.84 1.6532 2 0 0 6 56.46 42.78 1.6298 1 1 2 6 57.67 14.14 1.5984 2 0 1 6 59.02 1.56 1.5650 0 0 4 1 63.65 6.99 1.4619 2 0 2 6 66.05 1.53 1.4146 1 0 4 6 73.01 19.81 1.2958 2 0 3 6 76.18 6.56 1.2497 2 1 0 12 77.96 9.42 1.2256 2 1 1 12 79.13 3.00 1.2103 1 1 4 6 82.36 13.40 1.1709 1 0 5 6 83.25 5.58 1.1606 2 1 2 12 88.77 8.31 1.1022 3 0 0 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.