Ba2 Cu2.93 O7 Y Roth G, Heger G, Renker B, Pannetier J, Caignaert V, Hervieu M, Raveau B Physica C 153 (1988) 972-973 Crystallographic study of the tetragonal high-Tc superconductor YBa2(Cu.95Fe.05)3O7 _cod_database_code 1001379 _database_code_amcsd 0015012 CELL PARAMETERS: 3.8620 3.8620 11.6730 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 174.103 Density (g/cm3): 6.308 MAX. ABS. INTENSITY / VOLUME**2: 167.8983347 RIR: 8.667 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.57 1.77 11.6730 0 0 1 2 15.18 1.75 5.8365 0 0 2 2 22.86 3.41 3.8910 0 0 3 2 23.03 6.40 3.8620 1 0 0 4 27.70 7.55 3.2207 1 0 2 8 32.67 100.00 2.7410 1 0 3 8 32.80 51.81 2.7308 1 1 0 4 36.32 2.30 2.4735 1 1 2 8 38.56 6.15 2.3346 0 0 5 2 38.67 6.27 2.3283 1 0 4 8 40.35 12.10 2.2353 1 1 3 8 46.69 8.08 1.9455 0 0 6 2 47.06 29.98 1.9310 2 0 0 4 51.50 3.52 1.7745 1 1 5 8 52.68 1.19 1.7375 1 0 6 8 52.94 1.45 1.7297 2 0 3 8 53.02 1.45 1.7271 2 1 0 8 55.07 1.24 1.6676 0 0 7 2 55.48 1.92 1.6561 2 1 2 16 58.23 14.60 1.5845 1 1 6 8 58.46 33.85 1.5786 2 1 3 16 62.41 4.62 1.4880 2 0 5 8 62.49 2.57 1.4863 2 1 4 16 65.60 1.95 1.4232 1 1 7 8 68.46 8.71 1.3705 2 0 6 8 68.75 7.95 1.3654 2 2 0 4 68.78 3.69 1.3650 1 0 8 8 75.30 1.78 1.2621 2 0 7 8 77.66 2.36 1.2295 1 0 9 8 78.21 6.53 1.2222 3 0 3 8 78.28 6.87 1.2213 3 1 0 8 81.70 1.79 1.1786 2 2 5 8 82.84 2.15 1.1652 3 1 3 16 87.23 4.10 1.1176 2 2 6 8 87.25 2.13 1.1174 1 0 10 8 87.52 3.47 1.1146 2 1 8 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.