Ca0.5 Cu2 O6.3 Pb0.46 Sr2.46 Y0.5 Rouillon T, Provost J, Hervieu M, Groult D, Michel C, Raveau B Physica C 159 (1989) 201-209 Superconductivity up to 100 K in lead cuprates: A new superconductor Pb.5 Sr2.5 Y.5 Ca.5 Cu2 O7-delta _cod_database_code 1001412 _database_code_amcsd 0015015 CELL PARAMETERS: 3.8170 3.8170 11.9070 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 173.479 Density (g/cm3): 5.773 MAX. ABS. INTENSITY / VOLUME**2: 106.2490441 RIR: 5.992 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 22.40 5.63 3.9690 0 0 3 2 23.30 1.01 3.8170 1 0 0 4 24.49 4.28 3.6348 1 0 1 8 27.76 27.95 3.2133 1 0 2 8 30.02 2.22 2.9767 0 0 4 2 32.55 100.00 2.7512 1 0 3 8 33.19 71.13 2.6990 1 1 0 4 34.06 4.59 2.6322 1 1 1 8 37.78 14.09 2.3814 0 0 5 2 38.35 13.43 2.3473 1 0 4 8 44.86 2.24 2.0204 1 0 5 8 45.36 12.67 1.9995 1 1 4 8 45.72 4.33 1.9845 0 0 6 2 47.65 36.77 1.9085 2 0 0 4 51.15 12.58 1.7857 1 1 5 8 51.93 3.19 1.7607 1 0 6 8 53.26 1.72 1.7200 2 0 3 8 53.90 2.36 1.7010 0 0 7 2 56.04 7.05 1.6409 2 1 2 16 57.35 1.33 1.6066 2 0 4 8 57.66 7.16 1.5988 1 1 6 8 58.89 30.74 1.5681 2 1 3 16 59.50 4.26 1.5537 1 0 7 8 62.35 9.85 1.4893 2 0 5 8 62.39 1.78 1.4884 0 0 8 2 62.75 4.75 1.4808 2 1 4 16 64.78 2.27 1.4391 1 1 7 8 67.51 1.11 1.3874 2 1 5 16 67.55 3.01 1.3867 1 0 8 8 68.17 4.09 1.3756 2 0 6 8 69.68 9.10 1.3495 2 2 0 4 72.53 1.80 1.3033 1 1 8 8 73.13 1.94 1.2941 2 1 6 16 74.76 2.76 1.2698 2 0 7 8 76.57 1.21 1.2442 3 0 2 8 79.03 5.48 1.2116 3 0 3 8 79.39 7.93 1.2070 3 1 0 8 79.56 3.05 1.2049 2 1 7 16 80.92 1.51 1.1880 1 1 9 8 82.08 3.63 1.1741 2 2 5 8 82.12 2.63 1.1737 2 0 8 8 86.82 2.69 1.1218 2 1 8 16 87.13 2.23 1.1186 3 1 4 16 87.39 1.75 1.1159 2 2 6 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.