Ba0.9 Bi0.1 F2.1 Soubeyroux J, Reau J, Wahbi M, Senegas, Soo S Solid State Communications 82 (1992) 63-70 Neutron diffraction investigation of the Ba1-xBixF2-x solid solution _cod_database_code 1008590 _database_code_amcsd 0016481 CELL PARAMETERS: 6.1557 6.1557 6.1557 90.000 90.000 90.000 SPACE GROUP: Fm3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 233.256 Density (g/cm3): 5.250 MAX. ABS. INTENSITY / VOLUME**2: 220.3119230 RIR: 13.664 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 25.06 100.00 3.5540 1 1 1 8 29.01 29.07 3.0779 2 0 0 6 41.49 58.43 2.1764 2 2 0 12 49.08 43.41 1.8560 3 1 1 24 51.42 7.11 1.7770 2 2 2 8 60.13 7.78 1.5389 4 0 0 6 66.17 14.99 1.4122 3 3 1 24 68.12 8.08 1.3765 4 2 0 24 75.69 13.52 1.2565 4 2 2 24 81.20 7.39 1.1847 5 1 1 24 81.20 2.35 1.1847 3 3 3 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.