Behoite
      Jacobs H, Niemann A, Kockelmann W
      Zeitschrift fur Anorganische und Allgemeine Chemie 631 (2005) 1247-1254
      Low temperature investigations of hydrogen bridge bonds in the hydroxides
      beta-Be(OH)2 and epsilon-Zn(OH)2 by Raman-spectroscopy as well as X-ray and neutron diffraction
      Locality: synthetic
      Sample: T = 50 K
      _database_code_amcsd 0015822

      CELL PARAMETERS:    4.5260   4.6318   7.0192   90.000   90.000   90.000
      SPACE GROUP: P2_12_12_1
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    147.147
      Density (g/cm3):      1.942
      MAX. ABS. INTENSITY / VOLUME**2:      5.133795268    
      RIR:      0.861
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                23.01         68.25        3.8660    0   1   1         4
                23.39         53.61        3.8038    1   0   1         4
                25.38          1.12        3.5096    0   0   2         2
                30.41         27.18        2.9396    1   1   1         4
                32.00          1.43        2.7973    0   1   2         4
                32.28         30.58        2.7735    1   0   2         4
                37.81        100.00        2.3795    1   1   2         4
                38.89          2.59        2.3159    0   2   0         2
                39.83          6.98        2.2630    2   0   0         2
                41.04         20.13        2.1993    0   2   1         4
                41.95          3.32        2.1538    2   0   1         4
                43.33          1.46        2.0884    0   1   3         4
                43.54          4.25        2.0784    1   0   3         4
                44.56          7.17        2.0333    2   1   0         4
                45.87         18.38        1.9781    1   2   1         4
                46.50         20.60        1.9530    2   1   1         4
                47.83          1.07        1.9019    2   0   2         4
                47.98         15.07        1.8963    1   1   3         4
                51.40          9.05        1.7776    1   2   2         4
                51.98          2.14        1.7594    2   1   2         4
                52.12          2.95        1.7548    0   0   4         2
                56.04          7.17        1.6410    0   1   4         4
                56.22          1.33        1.6361    1   0   4         4
                56.58          4.83        1.6266    2   0   3         4
                56.89          2.34        1.6186    2   2   0         4
                58.52          3.80        1.5772    2   2   1         4
                59.79          3.34        1.5468    1   2   3         4
                60.31          3.53        1.5347    2   1   3         4
                65.02          1.25        1.4345    3   1   0         4
                65.22          3.19        1.4306    1   3   1         4
                66.53          2.68        1.4054    3   1   1         4
                66.90          2.05        1.3986    0   2   4         4
                67.55          2.43        1.3867    2   0   4         4
                69.71          2.23        1.3490    1   3   2         4
                70.47          1.04        1.3363    1   2   4         4
                70.94          3.86        1.3285    2   1   4         4
                70.98          2.48        1.3279    3   1   2         4
                73.49          2.25        1.2887    0   3   3         4
                74.38          4.06        1.2754    2   3   0         4
                74.89          4.88        1.2679    3   0   3         4
                75.81          1.80        1.2548    2   3   1         4
                76.58          1.54        1.2441    3   2   1         4
                76.93          4.60        1.2394    1   3   3         4
                79.91          3.74        1.2005    0   2   5         4
                80.78          2.34        1.1897    2   2   4         4
                80.81          5.10        1.1893    3   2   2         4
                83.27          1.10        1.1604    1   2   5         4
                83.72          2.42        1.1552    2   1   5         4
                84.87          1.55        1.1425    0   4   1         4
                85.79          1.62        1.1326    1   0   6         4
                87.28          1.09        1.1171    4   0   1         4
                88.97          1.63        1.1002    1   1   6         4
                89.07          1.30        1.0992    4   1   0         4
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.