Fabriesite Hansen S, Faelth L Zeolites 2 (1982) 162-166 X-ray study of the nepheline hydrate I structure Locality: synthetic _database_code_amcsd 0019785 CELL PARAMETERS: 16.4260 15.0140 5.2235 90.000 90.000 90.000 SPACE GROUP: Pna2_1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 1288.219 Density (g/cm3): 2.345 MAX. ABS. INTENSITY / VOLUME**2: 7.962742060 RIR: 1.105 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.77 48.72 8.2130 2 0 0 2 11.79 45.69 7.5070 0 2 0 2 15.99 18.57 5.5411 2 2 0 4 18.78 1.02 4.7249 1 1 1 4 20.15 90.72 4.4076 2 0 1 2 20.78 1.29 4.2737 2 3 0 4 21.64 3.59 4.1065 4 0 0 2 22.45 1.18 3.9610 4 1 0 4 23.40 2.93 3.8009 2 2 1 4 26.10 100.00 3.4139 2 4 0 4 27.63 2.36 3.2283 4 0 1 2 30.13 70.41 2.9657 4 2 1 4 31.30 23.87 2.8577 2 4 1 4 34.34 37.37 2.6117 0 0 2 1 36.72 34.68 2.4476 4 4 1 4 37.08 16.51 2.4248 6 0 1 2 38.09 3.49 2.3625 2 2 2 4 39.04 6.24 2.3074 6 2 1 4 40.80 4.83 2.2118 6 4 0 4 40.95 5.98 2.2038 4 0 2 2 41.50 3.46 2.1761 2 6 1 4 42.15 2.18 2.1438 0 4 2 2 42.76 3.12 2.1146 4 2 2 4 43.63 5.53 2.0743 2 4 2 4 44.11 3.01 2.0533 8 0 0 2 45.88 3.55 1.9778 4 6 1 4 47.59 2.76 1.9109 8 0 1 2 47.86 1.61 1.9004 4 4 2 4 48.15 4.34 1.8897 6 0 2 2 48.51 16.17 1.8767 0 8 0 2 49.20 3.42 1.8519 8 2 1 4 49.34 3.16 1.8470 6 6 0 4 50.51 5.10 1.8069 0 6 2 2 50.68 1.16 1.8014 8 4 0 4 51.81 3.19 1.7647 2 6 2 4 52.55 8.91 1.7414 6 6 1 4 53.03 1.14 1.7267 2 8 1 4 53.70 1.33 1.7069 4 8 0 4 53.82 5.96 1.7033 2 0 3 2 53.83 2.42 1.7029 8 4 1 4 55.57 2.32 1.6538 4 6 2 4 57.06 7.74 1.6142 8 0 2 2 57.43 2.30 1.6046 10 2 0 4 58.11 4.09 1.5873 8 6 0 4 58.91 10.00 1.5677 4 2 3 4 59.61 1.26 1.5511 2 4 3 4 60.77 4.46 1.5241 0 8 2 2 61.01 1.36 1.5187 8 6 1 4 61.63 6.44 1.5048 10 4 0 4 62.59 6.71 1.4841 6 8 1 4 62.93 1.09 1.4769 2 10 0 4 63.06 8.76 1.4742 4 4 3 4 63.30 5.15 1.4692 6 0 3 2 64.64 1.22 1.4418 6 2 3 4 67.34 1.05 1.3905 10 0 2 2 67.63 2.37 1.3853 8 8 0 4 68.65 1.99 1.3672 10 2 2 4 68.98 9.48 1.3614 4 10 1 4 69.27 2.04 1.3564 8 6 2 4 69.66 1.29 1.3498 4 6 3 4 70.75 1.48 1.3316 6 8 2 4 71.21 1.45 1.3241 12 0 1 2 72.36 2.53 1.3059 0 0 4 1 72.49 7.74 1.3039 10 4 2 4 73.42 1.29 1.2897 2 0 4 2 73.69 3.62 1.2856 2 10 2 4 74.30 2.11 1.2765 6 10 1 4 74.96 3.19 1.2670 6 6 3 4 76.02 2.38 1.2519 8 4 3 4 76.25 2.90 1.2487 12 4 1 4 76.82 1.32 1.2408 4 10 2 4 78.09 4.08 1.2238 8 8 2 4 78.40 2.06 1.2197 2 4 4 4 82.72 1.56 1.1666 4 12 1 4 83.50 1.21 1.1577 0 6 4 2 83.58 3.17 1.1569 6 8 3 4 83.86 1.23 1.1537 12 4 2 4 84.66 2.90 1.1448 14 0 1 2 88.16 1.56 1.1082 10 10 0 4 88.79 1.20 1.1019 8 0 4 2 89.42 4.35 1.0958 4 10 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.