Gismondine
Artioli G, Rinaldi R, Kvick A, Smith J V
Zeolites 6 (1986) 361-366
Neutron diffraction structure refinement of the zeolite gismondine at 15 K
Locality: synthetic
Sample: T = 15 K
_database_code_amcsd 0015867
10.011 10.614 9.853 90 93.11 90 P2_1/c
atom      x      y      z  occ Uiso
Ca   .71243 .07174 .35977      .111
Al1  .09783 .11445 .16605      .059
Al2  .58866 .86492 .14799      .056
Si1  .41701 .11342 .18365      .052
Si2  .90696 .87029 .16244      .049
O1   .08594 .16268 .99653      .080
O2   .26410 .08016 .21490      .079
O3   .43831 .14684 .02648      .070
O4   .24580 .40345 .30058      .077
O5   .99985 .98818 .20919      .086
O6   .04313 .24651 .25317      .070
O7   .47039 .22764 .28039      .075
O8   .51143 .99265 .22922      .070
Ow1  .25843 .10659 .49653      .100
H11  .20848 .31767 .01194      .175
H12  .26257 .09735 .39871      .157
Ow2  .59508 .13096 .55060      .093
H21  .53278 .29830 .03790      .157
H22  .56213 .41867 .12553      .152
Ow3  .90921 .11782 .49859      .105
H13  .97987 .17930 .47756 .384 .153
H23  .94105 .42852 .07771      .197
H33  .96046 .30710 .00027 .616 .115
Ow4  .77553 .23209 .23491 .697 .114
H14  .72229 .28729 .17445 .613 .159
H24  .86970 .25232 .22989 .697 .153
H34  .65855 .27923 .19458 .084 .164
Ow5  .73447 .32137 .41318 .303 .128
H15  .76015 .15794 .00480 .303 .209
H25  .74585 .39881 .35918 .303 .191
Ow6  .77947 .19590 .16474 .303 .142
H16  .73394 .26797 .14126 .303 .217
H26  .87648 .22894 .19538 .303 .220